2LiBH_4-MgH_2体系储氢性能的研究 【摘要】 LiBH4配位氢化物拥有很高的氢含量(18.5 wt.%,121 kg-H2/m3),是一种潜在的高容量储氢材料,但由于它的热力学性质稳定、放氢动力学缓慢以及吸放氢循环可逆性较差,因而限制了它的实际应用。本文在综述国内外LiBH4储氢材料研究进展的基础上,选择2LiBH4-MgH2体系作为研究对象,详细地研究了不同放氢条件下2LiBH4-MgH2体系的放氢路径与MgB2产物的形成机理,系统地考察了不同氟化物添加剂对2LiBH4-MgH2体系储氢性能的影响规律及其催化改性机理。对2LiBH4-MgH2体系放氢路径与MgB2形成机理的研究表明2LiBH4-MgH2体系存在两种不同的放氢路径DPL (Dehydrogenation pathway under low-pressure)和DPH (Dehydrogenation pathway under high-pressure)。当在较低的初始氢背压下放氢(DPL)时,LiBH4和MgH2会独自发生分解,生成LiH、B、Mg和H2,没有MgB2生成；而在较高的初始氢背压下放氢(DPH)时,LiBH4的自行分解受到抑制,MgH2会先行分解...?更多还原 【Abstract】 LiBH4, which owns high gravimetric and volumetric hydrogen densities (18.5 wt.% and 121 kg·H2/m3), has been regarded as one of the most promising hydrogen storage materials. However, LiBH4 is thermodynamically stable and kinetically slow, and it is required for extremely rigorous temperature and pressure conditions to reverse. So, it is limited for practical use. Based on the comprehensive review of the research and development of LiBH4 complex hydrides as hydrogen storage materials,2LiBH4-MgH2 ...?更多还原 【关键词】 配位氢化物； 2LiBH4-MgH2； 低氢压放氢路径(DPL)； 高氢压放氢路径(DPH)； 氟化物添加剂； 催化机理； 【Key words】 complex hydride； 2LiBH4-MgH2； DPL(dehydrogenation pathway under； lower-pressure)； DPH(dehydrogenation pathway under higher-pressure)； fluoride additives； catalytic mechanism； 摘要 6-8 Abstract 8-9 第一章 绪论 14-18 1.1 氢能及其应用 14 1.2 储氢技术的研究现状 14-18 1.2.1 物理储氢方式 15-16 1.2.2 化学储氢方式 16-18 第二章 文献综述:LiBH_4配位氢化物储氢材料的研究进展 18-32 2.1 LiBH_4的物理性质及空间结构 18-19 2.2 LiBH_4的储氢性能 19-22 2.2.1 LiBH_4的放氢性能 19-21 2.2.2 LiBH4_的放氢后的吸氢性能 21-22 2.3 LiBH_4储氢性能的改善途径 22-28 2.3.1 反应物失稳法 22-24 2.3.2 催化剂改性 24-25 2.3.3 纳米约束法 25-26 2.3.4 离子替换法 26-28 2.3 2LiBH_4-MgH_2体系研究进展 28-30 2.4 本文的研究思路及主要研究内容 30-32 第三章 实验方法 32-36 3.1 样品制备 32 3.1.1 实验原料 32 3.1.2 样品制备 32 3.2 储氢性能测试 32-34 3.2.1 储氢性能测试系统及空容标定 32-34 3.2.2 储氢性能测试 34 3.3 材料的组织与微观结