Ca2+比值對CO2局部腐蚀的影响.docVIP

PAGE PAGE 1 Ca2+/比值对CO2局部腐蚀的影响 杜新燕1 黄淑菊2 武博2 张建勋2 （克拉玛依市科比技术有限责任公司 新疆 834003；2西安交通大学焊接研究所 西安 710049） 摘要：本文研究了20＃试样半浸在65℃，通入0.1MPa压力的CO2气体，含两种K值（K＝Ca2+/）的模拟油气田产出水中，以及悬挂在该产出水形成的气相中的腐蚀行为。研究结果表明，K值为193（高K值）的平均腐蚀速率小于K值为87（低K值）的平均速率，而高K值下的局部扩展速率高于低K值下的局部扩展速率，即K值是影响CO2腐蚀的重要参数之一。 关键词：20#钢； CO2腐蚀；Ca2+/比值；平均腐蚀速率；局部腐蚀速率。 中国分类号：TG172 Influence of ratio of Ca2+/ on the CO2 corrosion Abstract: We have studied the CO2 corrosion behaviours of 20# steel samples,which were half-immersed in the simulated HYPERLINK .hk/translate?hl=zh-CNlangpair=zh-CN|enu=/article/info/2010012017006.htmlprev=/translate_s%3Fhl%3Dzh-CN%26q%3D%25E4%25BA%25A7%25E5%2587%25BA%25E6%25B0%25B4%26sl%3Den%26tl%3Dzh-CN oilfield produced waters?and were hung over the waters.The waters were with two K values(K= ratio of Ca2+/ )and with the 0.1 MPa CO2 gas , at 65℃.The results showed that the uniform corrosion rate of the samples with K=193 is more lower than that with K=87, but localized corrosion rate of the samples with K=193 is more higher than that with K=87. Immediately, the K value is one of the key Parameters infuence on the CO2 corrosion. Key word: 20＃steel;CO2 corrosion; the value of Ca2+/,unifom corrosion rate,localized corrosion rate 1. 引言 油气集输管道输送的油气流体往往含有产出水和CO2气体，当CO2分压（Pco2）0.021MPa后，这种湿的流体可能引起集输管道的CO2腐蚀。油气集输管道CO2腐蚀失效形式的调研表明，孔蚀和沟槽腐蚀等局部腐蚀是最常见的局部腐蚀形式[1-2]，而目前预测CO2腐蚀的模型大多适用于全面腐蚀[3-4]，可见预测CO2局部腐蚀失效的研究是很重要的。 Crolet J L等人根据对油气井CO2腐蚀原因的研究，提出以产出水中的Ca2+/比值（以下以K值表示）来预测CO2引起孔蚀等局部腐蚀倾向的观点。根据他们的观点，K值在0.5～1000范围内，油气井设备发生局部腐蚀的倾向大[5]。姚晓在分析6起我国油气井的CO2腐蚀事故的原因时，也支持Crolet J L等人的上述观点[6]。关于在油气田产出水成分的调研表明，K值在0.5～1000之间属于常见情况，可是目前缺少就K值处在0.5～1000范围之间对CO2腐蚀影响的研究，所以本文选定了K比值在0.5～1000之间的两个数值，研究K值的变化对CO2腐蚀的影响。 2．试验方法和条件 单井、支线等油气田集输管道通常以20＃钢制造，本文也选20＃钢为试验材料。测试腐蚀速率的试样加工成30×15×3 mm的片状小试样。为了获取沟槽腐蚀的信息，选择了大试样。大试样为长度是80mm，外径为25.4mm的无缝钢管（管的内壁以胶管密封），半浸泡于溶液中。三个小试样置于气相介质中，见图1。试样经过150＃～400＃砂纸擦磨，小试样在分析天平称重后置于干燥器中待用。 模拟产出水的溶液配方示于表1，根据K值的大小，试验溶液分成低K值和高K值两组，见表1。另外，为了对比Cl－离子和K值对CO2腐蚀的影响，也进