Hydrogen sorage alloy of Mg 2 Ni produced from Mg and Ni ultrafine particles.docVIP

下载本文档

2
0
约1.11万字
约 9页
2016-11-29 发布于贵州
举报
版权申诉

Hydrogen sorage alloy of Mg 2 Ni produced from Mg and Ni ultrafine particles.doc

1、原创力文档（book118）网站文档一经付费（服务费），不意味着购买了该文档的版权，仅供个人/单位学习、研究之用，不得用于商业用途，未经授权，严禁复制、发行、汇编、翻译或者网络传播等，侵权必究。。
2、本站所有内容均由合作方或网友上传，本站不对文档的完整性、权威性及其观点立场正确性做任何保证或承诺！文档内容仅供研究参考，付费前请自行鉴别。如您付费，意味着您自己接受本站规则且自行承担风险，本站不退款、不进行额外附加服务；查看《如何避免下载的几个坑》。如果您已付费下载过本站文档，您可以点击这里二次下载。
3、如文档侵犯商业秘密、侵犯著作权、侵犯人身权等，请点击“版权申诉”（推荐），也可以打举报电话：400-050-0827(电话支持时间：9:00-18:30)。
4、该文档为VIP文档，如果想要下载，成为VIP会员后，下载免费。
5、成为VIP后，下载本文档将扣除1次下载权益。下载后，不支持退款、换文档。如有疑问请联系我们。
6、成为VIP后，您将拥有八大权益，权益包括：VIP文档下载权益、阅读免打扰、文档格式转换、高级专利检索、专属身份标志、高级客服、多端互通、版权登记。
7、VIP文档为合作方或网友上传，每下载1次，网站将根据用户上传文档的质量评分、类型等，对文档贡献者给予高额补贴、流量扶持。如果你也想贡献VIP文档。上传文档

Hydrogen storage alloy of Mg2Ni produced from Mg and Ni ultrafine particles The State Key Laboratory of Rare Earth Materials Chemistry and Applications, Peking University, Beijing 100871, China Yuejun Yu Abstract: Mg and Ni ultrafine particles were produced by hydrogen plasma metal reaction method, then mixed in the molar ratio of 2:1 and heated in Ar flow atmosphere to get Mg2Ni compound. Structure and hydrogen storage properties of the compound were measured. There are some features about this method: (a) The particles are mixed just by ultrasonic homogenizer, (b) The heating temperature is lower than that in chemical literature and, (c) The process of compound preparation is without hydrogen. This new method has advantages such as short process time, simple equipment and high product purity. The hydrogen absorption rate was enhanced and the plateau pressure was lowered greatly. Keywords: Mg2Ni, ultrafine particles, hydrogen plasma metal reaction, and hydrogen storage alloy. Introduction Mg-based hydrogen storage alloys are always attractive to many investigators, though the hydriding and dehydriding kinetics of Mg are slow and the hydride is too stable for most practical applications. Mg rich intermetallic alloys are being investigated in order to determine the optimum composition leading to the best-reversible hydrogen absorption properties. Among them, Mg2Ni is the most intensively studied compound due to its low specific weight and cost [1]. Several fabrication techniques have been developed to produce nano-scale Mg2Ni, and the typical one is the energetic ball milling of hydrides. But its shortcomings are: the impurity is high, the process time is long, and the product is not uniformity, as a result, application of the method is limited. Nomura et al. [4] and Reily et al. [5] investigated formation of Mg2Ni by heat-treatment of Mg and Ni powder and found that it was possible to get the compound. However, temperature for the treatment was must el