OMMT和MH对PS 刘继纯，付梦月，李晴媛 （河南科技大学化工与制药学院，高分子科学与纳米技术重点实验室，河南 洛阳 471003） 摘 要： 将聚苯乙烯树脂与有机蒙土(OMMT)氢氧化镁(Magnesium Hydroxide, MH) 直接进行熔融复合制备PS/MH/OMMT复合材料，通过X射线衍射(XRD)对复合材料的微观结构进行了分析。结果表明：OMMT熔融复合后，片层间距增，与PS分子链形成了插层复合结构OMMT与MH阻燃性能更好关键词：聚苯乙烯；氢氧化镁；有机蒙脱土；协同作用；阻燃性能Flame Retardancy of PS LIU Ji-chun， FU Meng-yue， LI Qing-yuan， ZHANG Yu-qing (School of Chemical Engineering Pharmaceutics, Key Laboratory of Polymer Science and Nanotechnology, Henan University of Science and Technology, Luoyang, 471003, China) Abstract: The composites of PS/MH/OMMT were prepared by melt blending of PS resin, organically modified montmorillonite (OMMT) and surface modified magnesium hydroxide (MH). The structure of the composites was analyzed by X-ray diffraction. The flame-retardant property of the composites was investigated by employing horizontal burning, oxygen index and high temperature treatment methods. It was found that the interlayer space of OMMT is increased from 1.46 nm to 3.30 nm after melt blending with PS, indicating the PS chains are intercalated between the OMMT layers and the introduction of MH doesn’t affect the formation of the intercalation structure. The coexistence of OMMT and MH can decrease the melt dripping and smoke emitting of the composites in case of burning noticeably. The PS/MH/OMMT composite exhibits better stability and flame retardancy than its PS/MH counterpart. As a result, the amount of flame retardants can be greatly decreased. Key words: polystyrene; magnesium hydroxide; organically modified montmorillonite; synergistic effect; flame retardancy; 聚苯乙烯(PS) 因具有良好的透明性、尺寸稳定性、电绝缘性能和加工性能而广泛应用。但是，PS 非常容易燃烧，燃烧过程中滴严重且释放大量黑烟，因此对其进行阻燃、抑烟处理以提高应用的安全性是十分必要的。氢氧化镁(MH) 作为一种常用的无卤阻燃剂具有原料来源广泛、价格低廉、热稳定性好、不挥发、不析出不产生有毒气体、不腐蚀加工设备、消烟作用明显等诸多优点而备受关注，其主要缺点是与基体树脂的相容性较差，而且通常需要较大的添加量才能获得适宜的阻燃效果，这会使材料的力学性能下降、加工性能变差，因此，使用前需要对其进行适当的表面处理，与其他阻燃剂配合使用以减少其量[1]。把层状硅酸盐（例如蒙脱土(MMT)）引入到聚合物基体中，不仅能够改善聚合物基体的力学性能、气体阻隔性能及耐溶剂性能，而且还具有潜在的阻燃性和燃烧自熄特征，是一种环境友好的新型阻燃材料[2-4]。 本文利用熔融插层法制备了插层型PS/MH/OMMT复合材料，主要研究了