电站锅炉焊缝裂纹的检验分析[优化].docVIP

电站锅炉焊缝裂纹的检验分析 摘要：电站锅炉在运行当中，由于多种因素的影响会导致各种各样缺陷的产生，既有有关承压部件的，也有有关水汽质量的，针对汽包焊缝裂纹典型案例做好深入的分析，将有利于雷同缺陷及时、妥善处理。在役电站锅炉实际检验过程中，经常会遇到各种各样的实际检验问题，但归结起来主要有几类比较典型的情况。下面选取定期检验过程中发现及处理过的汽包焊缝裂纹案例，深入探讨了典型承压部件损坏的部位、损坏的原因、修理的具体方案等，对这类典型问题的深入研究，有助于雷同问题的及时、快速、正确处理，确保被检锅炉按期、安全的投入运行。本文通过分析一台中压电站锅炉锅筒内壁纵焊缝裂纹产生的原因,制订了裂纹消除工艺并对锅筒内壁纵焊缝裂纹进行了修复,同时提出了裂纹预防措施。 Power station boiler in operation,due to the influence of various factors can cause various defects,both related to bearing components, There is also related to water quality,the drum weld crack case do thorough Analysis,will be helpful for similar defects timely,appropriate processing.Boilers in service actual testing process,often encounter a variety of practical problems of testing,but mainly divides into several typical cases.The following selected regularly found during inspection and processed drum seam welding crack cases,discusses the typical pressure bearing parts damage,damage causes,repair the concrete scheme Of the typical problems,in-depth study,contribute to similar problems timely,rapid,correct processing,ensure boiler,seized on schedule safe operation.In this paper,through the analysis of medium pressure boiler drum wall longitudinal weld cracks reasons,formulate crack elimination technology of drum wall and the longitudinal weld seam crack was repaired,and puts forward the prevention measures of the crack. 关键词：电站锅炉 焊缝裂纹 检查分析 Power station boiler Weld crack Check analysis 目 录 封 面…………………………1. 论文题目…………………………2. 论文摘要…………………………2. 关 键 词…………………………2. 正 文…………………………4. 参考文献…………………………7. 锅炉检验中经常发现锅筒内部预埋件焊缝、汽水挡板焊缝存在裂纹，有时也发现下降管、给水套管、安全阀管座等焊缝存在裂纹，偶尔还发现锅筒对接焊缝存在裂纹。 该厂锅炉系1997年制造、安装，1998年投入使用，2007年8月停炉检验时，经磁粉和超声检测发现，汽包第2道环焊缝上部外侧坡口热影响区有一条明显的腐蚀氧化裂纹，裂纹长450mm、宽0.02mm，最深处达20-25dB，最浅处3dB，在第2条环焊缝上部内侧存在熔合线表面裂纹缺陷6处；其它焊缝也存在多处表面和埋藏缺陷，但未超标。分析表明：从开裂的第2条环焊缝，焊缝外观很不规则，焊缝比母材高出许多，形成了一个突变的台阶，在焊缝的融合线附近存在较多表面缺陷;这样，在锅炉频繁的启停中，汽包受到周期性的加热、冷却，在交变应力的作用下导致开裂，继而发展。鉴于上述情况，采用了