美国标准一个细节出错PCCP失效解析..docVIP

PCCP失效解析—美国结构设计标准一个细节有错 沈之基 (上海市自来水公司, 上海原水股份有限公司 200085) 摘要： PCCP主要失效模式是钢丝腐蚀管爆裂，防护层裂缝是钢丝腐蚀主要原因；防护层裂缝不可避免，产品结构设计中存在先天隐蔽性缺陷；高内压的大口径PCCP管线“膨胀量”大，特别危险。信息高度不对称，造成不公平的竞争环境和结果。美国主流的管道设计已经不再考虑PCCP。失效信息在中国慢慢传开，输水管线市场将出现大变局。 关键词： PCCP 、失效 、钢丝腐蚀 、砂浆防护层、防护层裂缝、断裂 、爆裂、 钢管 Parsing of PCCP failure--- A mistake in detail of American structure design standard Shen Zhi ji (SHANGHAI WATERWORKS CO., SHANGHAI?MUNICIPAL?RAW?WATER?CO.,LTD? 200085） Abstract： The main failure mode of PCCP is main pipe burst due to fracture of the prestressing wires caused by corrosion. The?cracking of mortar coating which is used to protect prestressing wire is inevitable. It is inherent and hidden defects in design concept. High internal pressure and large diameter pipeline is particular dangerous. Highly unbalanced information, caused the unfair competition environment and results. In the United States has, PCCP is no longer in the consideration for mainstream design of transmission mains. The failure information spread slowly, water pipeline market will begin to change。 Keywords: PCCP, failure, steel wire corrosion, mortar protective layer , protective layer crack, fracture, burst, steel pipe 0.前言 PCCP能够经济，其核心手段是采用高强度钢丝和预应力技术。钢丝的设计应力是钢管钢材的5倍以上，由此节约了钢材而取得经济性。 PCCP能够耐腐蚀，是因为主要受力元素---钢丝，有砂浆保护层保护。砂浆保护层能充分保护钢丝，这是发展这个产品时开发人员的期望，也是这个产品投入运行一段时间内的表现；但是随着时间推移，大量的管线运行实践表明，PCCP中钢丝容易腐蚀，其结果是管爆裂（1、2）。新构造的实际表现同开发期望有极大的差异。 1.主要失效模式是钢丝腐蚀管爆裂，防护层裂缝是钢丝腐蚀主要原因。 PCCP主要失效模式是爆裂，是钢丝腐蚀断裂引起，这已经得到大量运行实践证明并为行业公认。 钢丝腐蚀断裂原因，可以列举很多。因为腐蚀本质上是腐蚀电池或杂散电流运动结果，所以通常总会自然地将“土壤有腐蚀性介质（含杂散电流）、保护层裂缝”看成是钢丝腐蚀的二个必要条件和主要原因，是二者交集才发生腐蚀，这二个主要原因实际作用是怎么样的，哪一个实际作用更大一些，现在有二种观点。 1.1. 腐蚀性介质说 这种观点紧紧抓住腐蚀断裂是腐蚀电池或杂散电流运动结果这个事实，对土壤有腐蚀性介质、杂散电流特别看重，认为土壤有腐蚀性介质时，才需要采取对应措施。如果土壤没有腐蚀性介质等，那保护层即使有裂缝，裂缝处因砂浆提供了高碱性环境，钢丝表面被钝化而不会腐蚀，就不需要采用防腐蚀措施。 对策的重心也就自然针对腐蚀性介质：如采用环氧煤沥青涂覆管道外壁，加阴极保护措施；这种观点无论在理论上还是实践上，都可以认为是有效果、可操作的；但其最大不足是效力不高而且不彻底，做了这么多的努力，结果还是对钢丝的腐蚀不放心，还要再对运行中PCCP钢丝状况, 采取实时监测的措施，而这个实时监测的进行也需要化很大力气和费用。 中国现在以南水北调工程为主