从铌矿中直接制备铌镍合金粉前驱体试验研究.docVIP

从铌矿中直接制备铌镍合金粉前驱体试验研究 孙映，， （） 摘要：考察了磨矿粒度、焙烧温度、焙烧时间、酸矿比、硫酸浓度对铌浸出率的影响工艺参数：磨矿粒度温度300 ℃焙烧3 h、硫酸浓度10mol/L酸矿比2.5，在此下，浸出率可达到94% 关键：TF841.6 文献标志码：A 文章编号：1007-7545（2017）02-0000-00 Preparation of Nickel-Niobium Alloy Powder Precursor from Niobium Ore SUN Ying, HE Qi, LI Qiu-ju (State Key Laboratory of Advanced Special Steels, Shanghai University, Shanghai 200072, China) Abstract：Niobium-nickel alloy powder precursor NiNbO6 was prepared directly from niobium ore. Effects of grinding size, roasting temperature, roasting time, ratio of acid to ore, and sulfuric acid concentration on niobium leaching rate