HRB500钢筋的研制与生产分析.docVIP

HRB500钢筋的研制与生产分析 王学忠，刘佩明，穆国栋，路清祥，侯可强 （济南钢铁集团总公司，山东 济南250101） 摘　要：为调整小型材产品结构，扩大品种，推进建筑用钢筋的升级换代，满足市场对500MPa钢筋的需求，济钢利用微合金化技术，成功研制开发出HRB500钢筋混凝土用热轧带肋钢筋，实物质量达到了GB1499—1998的要求。为进一步改善提高钢筋的实物质量，对试验和批量生产的钢筋做了全面分析，提出了生产工艺具体技术要求。 关键词：HRB500；热轧带肋钢筋；产品开发；力学性能 中图分类号：TG335.6+4　　 文献标识码：A　　 文章编号：004-4620（2005）03-0020-03 Development and Production Analysis of HRB500 Reinforcing Bar WANG Xue-zhong, LIU Pei-ming, MU Guo-dong, LU Qing-xiang, HOU Ke-qiang （Jinan Iron and Steel Group Corporation，Jinan 250101，China） Abstract: HRB500 reinforcing bar was brought into the standard of National Construction Steel Material. In order to adjust production system, enlarge variety, upgrade the bars and meet the requirements of market, HRB500 hot rolled ribbed steel bar was developed successfully. It reached the requirements of GB1499—1998. For improving the bars quality, full analysis on experimentations and practical technical request were put forward. Key words：HRB500; hot rolled ribbed steel bar; production development; mechanical properties 1 前? 言 　　目前，世界各国的建筑已向大型化发展，为提高大型建筑物的安全性，国外建筑行业已普遍采用焊接性能好、强度高的钢筋，如西欧、北美主要使用强度较高的400MPa、500MPa级钢筋。1990年以后又开始进一步开发500MPa级钢筋，俄罗斯1993年钢筋产品标准增加了500MPa、600MPa级钢筋，美国1996年钢筋产品标准增加了520MPa级钢筋。为尽快赶上发达国家500MPa级钢筋的生产应用技术，实现我国建筑用钢筋的升级换代，济南钢铁集团总公司（简称济钢）研制成功500MPa钢筋，并形成批量生产能力，满足国内外市场的需求。 2 钢筋的研制 2.1 技术要求　　（1）执行标准：GB1499—1998；（2）牌号：HRB500；（3）技术要求：化学成分见表1，力学性能见表2。 表1? 标准及内控化学成分要求 % 标准 C Si Mn P S Ceq GB1499 ≤0.25 ≤0.80 ≤1.60 ≤0.045 ≤0.045 ≤0.54 内控 0.19~0.25 0.40~0.60 1.40~1.55 ≤0.040 ≤0.045 ≤0.52 表2? 力学性能要求 标准 公称直径/m σs/MPa σb/MPa δ5/% 弯心直径 GB1499 6~25 500 630 12 4a 28~50 5a 内控 6~25 520 640 14 4a 28~50 5a 　　碳当量Ceq（%）值可按式（1）计算： Ceq=C+Mn/6+（Cr+V+Mo）/5+（Cu+Ni）/15??? （1） 2.2 成分设计2.3.1 常规元素? 钢中每增加0.1%C，σs、σb可分别提高28MPa和70MPa，但对钢的塑性和焊接性能均不利。因此，要控制钢中的C含量，防止碳当量过高。Mn的加入可提高固溶强化效果，降低相变温度，细化钢的组织，提高强度及韧性，且Mn能提高Nb、V、Ti在奥氏体中的固溶度积，增强其沉淀强化效果。但含量太高会增加碳当量，不利于焊接。2.3.2 微合金元素? 通过比较，采用V微合金化，利用V在奥氏体中的固溶度积，增强其沉淀强化效果，保证钢的应变时效，降低脆性转变温度，使钢的强度和韧性获得较好的配合，可有效提高钢的高应变低周疲劳性能，尤其是在地震荷