新型工艺对汉麻纤维性能的影响.docVIP

新型工艺对汉麻纤维性能的影响 　　摘要：本文采用UV-辐射、冷冻骤热、生物酶处理和高温高压联合处理的新型工艺，对汉麻纤维进行脱胶处理，研究了其工艺条件对汉麻纤维残胶率、力学性能等的影响。利用扫描电镜（SEM）进行表面形貌观测、红外光谱法（FTIR）进行结构分析，热重分析仪（TG）进行热稳定性表征。结果表明：经上述新型工艺处理后汉麻纤维木质素含量由14.13%降低到0.71%，残胶率由43.12%降为2.26%，汉麻纤维表面胶质和杂质基本去除，纤维表面光滑，白度增加，纤维变细且均匀，力学性能优良，柔顺性好，热稳定性提高。且化学试剂用量减少1/3，有利于节能减排。 　　关键词：汉麻；高温高压；脱胶；残胶率 　　中图分类号：TS123 　　文献标志码：A 　　The Effect of New of Process on Hemp Properties 　　Abstract： In this paper， a new combined process that consists of UV-freezing-heating， enzyme-treatment and HTHP treatment was adopted for the degumming of hemp fiber， and the influence of different process conditions on residual gum rate and mechanical property was investigated. Hemp fibers before and after degumming were characterized by using SEM， FTIR and TG， the changes of overall performance and structure and chemical composition before and after degumming of hemp fiber were analyzed. It showed that the lignin content reduced to 0.71% from 14.13%， the residual gum rate reduced to 2.26% from 43.12%. The fiber has smooth surface， increased whiteness， reduced diameter but improved evenness as well as better mechanical property， compliance and thermal stability. . Chemical reagent dosage has reduced by about 1/3， which means energy conservation and emissions reduction. 　　Key words： hemp fiber； HTHP； degumming； residual gum rate 　　传统汉麻脱胶工艺一般采用天然水微生物脱胶、机械脱胶、化学脱胶等方法，天然水微生物脱胶周期长，效率低、劳动强度大，质量不稳定；而机械脱胶方法脱胶不彻底，一般用作预处理；化学脱胶则需要大量的水和化学药品，对环境不友好。因此亟待探索出一条污染少、能耗低、性价比高、可以大幅改善汉麻纤维性能和可纺性的工艺路线。 　　本文拟采用高温高压新型脱胶工艺对汉麻进行脱胶处理，并研究高温高压处理对汉麻脱胶及其性能的影响。 　　1 实验 　　1.1 主要实验材料 　　汉麻（河南固始产）；木质素酶（湖州美欣达生物科技有限公司），乳化剂（湖州美欣达生物科技有限公司），氢氧化钠（NaOH），双氧水（H2O2，30%），硫酸，硫酸镁，碳酸钠，三聚磷酸钠，亚硫酸钠，硫化钠等（化学试剂均为分析纯）。 　　1.2 主要实验仪器 　　高压蒸汽锅，DW-86L386型超低温保存箱，YG（B）003A型电子单纤维强力测试仪，JSM-6700F型场发射扫描电子显微镜，FTIR-1730型傅里叶红外光谱仪，STA 409 PC型同步热分析仪（TG-DTA）。 　　1.3 实验方法 　　脱胶工艺采用以下步骤： 　　（1）UV-辐射：将汉麻纤维放入NaOH（6g/L）、H2O2（6g/L）和助剂的溶液中，紫外辐射20min； 　　（2）冷冻骤热：紫外辐射后的汉麻纤维放入冷冻箱20 min，-55℃，然后放入沸水中骤热20min，再将汉麻纤维洗至pH值=7； 　　（3）将冷冻骤热后的纤维放入 8g/L的木质素酶溶液中，40℃，pH值=