La3+PbCrO4复合物的制备及其降解孔雀石绿的研究概要.doc

包头师范学院 本科毕业论文 二 〇 一 五 年 五 月 摘 要 本文分别通过热沸腾法、共沉淀法合成了PbCrO4掺杂La3+复合物可见光光催化剂，研究了La3+/PbCrO4在可见光照射下降解孔雀石绿的催化活性。本文通过改变La3+/PbCrO4的掺杂量、可见光照射时间、光照功率、催化剂的添加量、染料、烧样温度和烧样时间对降解率的影响，并且与单一的PbCrO4可见光光催化性能进行了对比。实验结果表明，加入La3+/PbCrO4之后降解率明显增加，掺杂后的光催化剂能更高效地对燃料废水进行讲解。 关键词: 稀土Abstract This paper through the hot boiling method, coprecipitation synthesis the PbCrO4 visible light catalyst, doping La3+ complex La3+/PbCrO4 in visible light irradiation was studied in the catalytic activity of malachite green. In this paper, by changing the amount of doping La3+/PbCrO4, visible light irradiation time, light power, adding amount of catalysts, dye, burning temperature and burning time influence on degradation rate, and with a single PbCrO4 visible light catalytic properties were compared. The experimental results show that the degradation rate increased significantly after join La3+/PbCrO4, after doping the photocatalyst can more efficiently to explain the fuel waste water. Key words: Rare earth; Lead chromate; Catalytic activity; Degradation rate; Malachite green 目 录 引 言 1 1 试验部分 2 1.1 仪器与试剂 2 1.1.1 主要仪器 2 1.1.2 主要试剂 2 1.2 药品制备 3 1.2.1 PbCrO4的制备 3 1.2.2 La3+/PbCrO4复合物的制备 3 1.3 实验方法 3 2 实验结果 4 2.1 不同温度下的La3+/PbCrO4对降解染料的影响 4 2.2 热处理时间对La3+/PbCrO4可见光光催化活性的影响 4 2.3 可见光光照功率对La3+/PbCrO4复合物光催化活性的影响 5 2.4 光照射时间对La3+/PbCrO4复合物和PbCrO4光催化活性的影响 6 2.5 染料溶液初始浓度对La3+/PbCrO4和PbCrO4复合物光催化活性的影响 6 2.6 La3+/PbCrO4和PbCrO4复合物光催化降解其它染料 7 2.7 催化剂的量对La3+/PbCrO4光催化活性的影响 8 结 论 8 参考文献 9 致 谢 10 引 言 随着我国工业化的飞速发展，%。生产工艺减排废水循环利用和废水处理系统优化是工业废水污染治理的基本途径［E］[10]。据环境保护部通报2009年，3486家国家重点监控企业的废水化学需氧量部分测次超标的占24 %，全年监测超标的占12 %。工业废水的治理做了许多有益的工作，但治理能力的增长还赶不上水体污染速度的增长，原因是多方面的，其中技术落后是主要原因之一。如物理法利用吸附剂表面活性将染料废水中的有机物和金属离子吸附并浓集于其表面膜超滤和反渗透分离达到净化水的目的。只是把污染物从一相转移到另一相，污染物本身并没有得到彻底降解。化学法通过使用化学药剂，在化学反应过程中对污染物进行氧化或者还原降解，改变污染物的形态，将它们变成无毒或微毒的新物质，或者转化成容易与水分离的形态，从而达到处理的目的。但这种方法需要大量的化学药剂，运行成本较高不适合大规模使用，同时，也可能产生二次污染。生物处理法是利用微生物代谢作用，使废水中的有机污染物和无机营养物转化为稳定、无害的物质，这是价格相对低廉、目前广泛采用的一种水处理方法，但是仍存在着，对有些有毒物质只能部分降解等。电化学