MoO的性能和应用.docVIP

MoO3的性能及应用 刘星，黄剑锋，曹丽云 （教育部轻化工助剂化学与技术重点实验室，陕西科技大学，材料科学与工程学院，陕西西安，710021） 摘要： 三氧化钼因其具有特殊结构，非常适合其它小分子或离子的嵌入而受到越来越多的关注。本文介绍了纳米三氧化钼的性能,如电致变色、光致变色、催化和气敏等，而导致这些性能的原因是三氧化钼独特的[MoO6]八面体层状结构。这种特殊的层状结构使三氧化钼在光电、抑烟/阻燃、催化、气敏材料等方面具有广阔的应用前景。 关键词：三氧化钼; 性能；应用。 中图法分类号：TB34 文献标识码： A The Property Application of MoO3 LIU Xing, HUANG Jian-feng, CAO Li-yun （Key Laboratory of Auxiliary Chemistry Technology for Chemical Industry, Ministry of Education, Shaanxi University of Science and Technology, The school of science and engineering, Xi’an,Shaanxi ,710021） Abstract Molybdenum trioxide has unusual structures, in which some small molecules and ions can easily be inserted to be concerned all the more in this paper. Also pointed out that nano-molybdenum trioxide with electrochromic, photochromic, catalysis, gas-sensing properties and so on, which led to these properties because molybdenum trioxide with unique eight noodles layered structure. It may be applied in many fields such as optical/electrical, suppression filling / flame retardant, catalysis, gas-sensor material and so on. The fields which molybdenum trioxide be applicated and development are reviewed. Key words molybdenum trioxide; properties; application 0 引言 MoO3是由金属原子Mo在中心、氧原子在角边的[MoO6]八面体为基本结构单元共角、形成链连接,每两个相似的链共边连接形成层状的MoO3化学计量结构,层与层之间靠范德华力作用而交错堆积排列。三氧化钼具有层状结构和框架是很重要的,其中存在着广延的通道,可用作离子的流通渠道和嵌入位置。开放的三氧化钼晶体结构和它的水化物都是H+、Li+及其他离子的良好离子注入主体。这一优良的特性使其在信息显示与储存、催化剂、传感器等领域具有广阔的应用前景[1-4]。 三氧化钼具有电致变色[5-7]、抑烟—阻燃性[8、]、催化降解[10、]以及气敏特性[12]等。下面就其几种氧化钼的性能和应用作一简述。 1 电致变色及其应用 电致变色是指物质在外加电压的感应下, 由于电场的原因,物质发生氧化－还原反应,导致物质的光吸收或光散射特性发生变化,继而引起其颜色的变化,而这种颜色的变化能够可逆地响应电场的变化, 其中MoO3的变色是通过Mo的变价引起光的吸收,电子和离子同时注入到晶格间隙产生着色，用方程式表示为： MoO3 + xA+ + xe-→AxMoO3 式中0 x 1，A+为Li+ 、H+ K+ 、Na+等。A+的注入使得部分Mo6+还原为Mo5+ ,电子e-吸收光子能量而处于激发态,在Mo5+与Mo6+离子能级之间迁移,电子迁移时吸收光子能量导致着色[13]。 制备性能优异的三氧化钼薄膜，一直是研究的重点。近年来 ,随着科学技术的进步，不断出现许多新型的三氧化钼薄膜制备方法。目前已有多种制备MoO3薄膜的方法，如蒸镀法[14、15][16]、溅射法[17]、溶胶—凝胶法[18、1]等。 表1 各种制备方法的比较 制备方法 优点 缺点 蒸镀法 设备简单，易于操作 制备的薄膜与基底结合不牢固，容易剥落，另外该制膜方法设备昂贵，技术