焙烧温度对耐磨钢纤维浇注料 性能的影响 摘要 本实验采用特级矾土熟料为主要原料，以高铝水泥为结合剂，钢纤维为外加剂，研究了不同焙烧温度对耐磨钢纤维浇注料的耐压强度、抗折强度、烧后线变化率及施工性能的影响。结论是耐压强度，抗折强度，烧后线变化率，密度随着焙烧温度的增高而降低。 关键词：耐磨钢纤维浇注料，焙烧温度，物理性能 Abstract This experiment adopts the special grade bauxite clinker as main raw materials, with high alumina cement as binder and steel fibre as admixture, studied different calcination temperature on the wear of steel fiber reinforced castable after compressive strength, flexural strength, burning rate and the influence of the construction. Conclusion is compressive strength, flexural strength, after firing line rate, density and decreased as the calcination temperature increased. Key words: Wear resistant steel fiber reinforced castable、Calcination temperature、physical properties 1.绪论 3 1.1不定型耐火材料概述 3 1.1.2不定型耐火材料组成 4 1.1.3不定性耐火材料制备技术 5 1.2钢纤维浇注料 6 1.2.1浇注料的简述 6 1.2.2钢纤维浇注料简述 7 1.2.3钢纤维的增强的原理 7 1.2.4钢纤维耐磨浇注料的性能 8 1.2.5影响耐磨钢纤维浇注料性能的主要因素 8 1.3实验原料 9 1.3.1特级矾土 9 1.3.2高铝水泥 10 1.4实验目的及意义 11 2实验过程 12 2.1实验原料 12 2.2实验设配 12 2.3实验方案 13 2.3.1耐火浇注料混料过程 13 2.3.2耐火浇注料的烘干 14 2.3.3耐火浇注料的焙烧 14 2.3.4耐火浇注料性能测试 15 2.4实验结果分析 19 2.4.1体积密度数据分析 19 2.4.2线变化率分析 20 2.4.3抗压强度分析 21 2.4.4抗折强度数据分析 22 3.结论 23 致谢 24 参考文献 25 1.绪论 1.1不定型耐火材料概述 　　不定型耐火材料品种繁多，由生产方法和使用方法可分为混凝土、浇注料、可塑料、捣打料、喷补料、投射料、涂抹料、干式捣打料、火泥料，各种补炉料(沥清结合大面补炉料、马丁砂等)也属于不定型之列。尽管不定型产品名称繁多，其典型生产方法可归为以下三种主要形式：（首行缩进二个字） 　　1．混凝土。混凝土技术出现的较早，它是不定型产品中的定型产品，热上窑炉有些部位如均热炉加热炉炉顶炉墙，回转窑的前后口圈、下料斜坡、卸料室墙壁等处，都町以设计成大形砌体(加热炉顶块重3-4吨)做成混凝土。混凝土的牛产方法，是将浇注料注入模型中，振动成型，脱模后热处理，提供给用户的除块大、体重之外，在使用上和机压砖没有本质区别。这种在生产厂家完成的浇注料用水量比现场浇注少10％以上，加工质量好，且质量稳定。由于砖大、重，现场须有起重吊装设备，只要现场可以吊装施工，应尽量采用混凝土，也可以做成稍小些形体，几个人能抬得动就行。混凝土不须用户做特殊的热处理，仪此一点就很有意义。（首行缩进二个字） 　　2．浇注料。浇注料是耐火材料厂提供原料和配料方案，现场加工，用振动棒密实，养护后须热处理，由于受现场条件限制质量不稳定，但浇注料的整体性好于混凝土，对浇注料质量至关重要的用水量和热处理两个方面不如混凝土，原料的消耗比混凝土多5％～8％。（首行缩进二个字） 　　3．可塑料。从生产方法上说可塑料介于混凝土和浇注料中间。它由耐火材料厂先将“浇注料”做成具有可塑性的泥条，配料中有缓凝剂，由塑料袋封装，在现场进行施工和热处理。可塑料施上中的最大问题是打结接茬处易起皮脱落，缓凝剂用量不当或是塑封不良易硬化结块。（首行缩进二个字） 1.1.2不定型耐火材料组成 ???????包括耐火骨料和粉料、结合剂、外加剂等。其用量应根据不定形耐火材料的不同品种和用途决定。一般情