船舶的腐蚀与防护讲义.docxVIP

船舶上材料保护研究进展 作 者 姓 名 卜祥星 专业 班级 材研1302 指导教师姓名 乔宁 学 号 2013200313 摘 要：船舶海上腐蚀是影响其寿命的最大因素之一。因腐蚀导致结构损坏和破坏，严重影响船舶性能和安全。本文介绍了当前船舶防腐蚀技术措施的实际应用情况。探讨在船体防腐蚀新技术的发展情况，如船体防腐涂料技术、防腐涂装技术、阴极保护功能和涂膜结合技术、防腐蚀监测新技术等方面的新技术应用。 关键词：船舶，防腐蚀新技术，阴极保护，防腐蚀检测 ABSTRACT： The ships marine corrosion is one of the biggest factors that affect its life span，The structure damage and the destruction caused by corrodes affects the ships performance and security seriously．This article introduces the practical application situation of the current ships corrosion preventing technology and methods，discusses the development situation of new hull anticorrosion technology and new technology application，such as the hull an corrosion painting technology ，the anticorrosion painting and camouflage technology ，the cathode protection function and the painting film combination technology ，the new anticorrosion monitor technology and so on． Key words: ship ,new technology of corrosion protection ,catholic protection, corrosion test 目前，大多数船舶都采用金属外壳。而金属在海洋环境中，受海水温度、海水含盐度、海洋大气温度、海洋大气湿度的影响，腐蚀程度很严重，腐蚀不仅降低了船舶钢结构的强度，缩短了船舶的使用寿命，同时还会使航行阻力增加，航速降低，影响使用性能[1]。更为严重的是，一旦出现穿孔或开裂，还会导致海损事故的发生，造成惊人的损失[2]。这已引起国内外防腐专家的极大关注，并积极研究探索解决金属腐蚀的各种防护技术方法和措施。 一、船舶腐蚀的类型及产生原因 船舶腐蚀发生的原因主要有以下几种： 1．船体在初次涂装时由于其表面处理不干净，存在残碱、残盐、残存氧化皮或锈斑等而引起的破坏作用。残碱对金属有较大的亲和势，即使在涂覆涂层后，它还能自发的沿着涂层与金属界面扩展而破??涂层与金属表面的粘附；残盐与通过涂层渗透进来的水分子发生水解和受氧分子的作用生成不溶性产物，此物质与金属形成腐蚀电池，体积不断增大，使涂膜破坏；残存氧化皮在介质发生渗透时，轧制氧化皮和轧制氧化皮缝隙所暴露出的铁，在电解质溶液下形成腐蚀电池，结果腐蚀沿缝隙在轧制氧化皮下扩展，最后氧化皮带着表面的涂层一起脱落[3]。 2．机械作用腐蚀。机械作用的腐蚀包括腐蚀作用和机械磨损，二者相互加速[4]。其中包括冲击腐蚀，这是由于液体湍流或冲击所造成；空泡腐蚀，高速流动的液体，因不规则流动，产生空泡，形成“水锤作用”，常常破坏金属表面的保护膜，加速腐蚀作用，如螺旋桨、泵轴等处易发生；微振磨损腐蚀，两个紧接着的表面相互振动而引起的磨捐；应力腐蚀开裂，在拉伸应力和腐蚀介质作用下的金属腐蚀破坏，金属内会产生沿晶或穿晶的裂纹[5]。 3．生物腐蚀。生物腐蚀是由海洋生物的船底附着物引起的，这种腐蚀包括化学腐蚀和电化学腐蚀两种[6]。由于海洋生物在船底的附着，破坏了漆膜，造成钢板局部电化学腐蚀；由于微生物的新陈代谢作用，分泌出具有侵蚀性的物质以及其他有机酸和无机酸引起钢板的腐蚀作用等[7]。 4．由于光照、温度、化学介质、磨损或机械损伤等原因引起的破坏。光照会使涂层老化、粉化；过高的温度以致超过高聚物所能承受的极限温度时会出现发软或龟裂、熔化等问题；化学介质会使涂层溶胀或溶解、脆化等；机械损伤会造成涂层破裂[8]。 5．介质渗透后使涂层下金属表面发生电化学腐