Effect of flame一front speed on the pisolite-ore sintering process.pdf

下载文档

8
0
约3.63万字
约 8页
2017-04-13 发布于江苏
举报
版权申诉
保障服务

Effect of flame一front speed on the pisolite-ore sintering process.pdf

1、本文档共8页，可阅读全部内容。
2、原创力文档（book118）网站文档一经付费（服务费），不意味着购买了该文档的版权，仅供个人/单位学习、研究之用，不得用于商业用途，未经授权，严禁复制、发行、汇编、翻译或者网络传播等，侵权必究。
3、本站所有内容均由合作方或网友上传，本站不对文档的完整性、权威性及其观点立场正确性做任何保证或承诺！文档内容仅供研究参考，付费前请自行鉴别。如您付费，意味着您自己接受本站规则且自行承担风险，本站不退款、不进行额外附加服务；查看《如何避免下载的几个坑》。如果您已付费下载过本站文档，您可以点击这里二次下载。
4、如文档侵犯商业秘密、侵犯著作权、侵犯人身权等，请点击“版权申诉”（推荐），也可以打举报电话：400-050-0827(电话支持时间：9:00-18:30)。

Effect of flame一front speed on the pisolite-ore sintering process

lable at ScienceDirect Applied Thermal Engineering 75 (2015) 307e314Contents lists avaiApplied Thermal Engineering journal homepage: www.elsevier .com/locate/apthermengEffect of flame-front speed on the pisolite-ore sintering process Hao Zhou*, Zihao Liu, Ming Cheng, Ruipeng Liu, Kefa Cen State Key Laboratory of Clean Energy Utilization, Institute for Thermal Power Engineering, Zhejiang University, Hangzhou 310027 PR Chinah i g h l i g h t s Influence of flame-front speed on sinter quality of pisolite ore is investigated. We examine the influence of flame-front speed on melting, reshaping, and coalescence. We discuss factors controlling flame-front speed in iron ore sintering process. The flame-front speed is proportional to fuel-combustion rate.a r t i c l e i n f o Article history: Received 9 January 2014 Accepted 19 September 2014 Available online 28 September 2014 Keywords: Pisolite ore Flame-front speed Sintering* Corresponding author. Tel.: t86 571 fa E-mail addresses: zhouhao@, itpep /10.1016/j.applthermaleng.2014.09.05 1359-4311/? 2014 Elsevier Ltd. All rights reserved.a b s t r a c t Flame-front speed has a large influence on sinter quality and production. To study the influence of flame- front speed on pisolite-ore sintering, five tests were conducted in a laboratory sinter pot. Through varying mix moisture, flame-front speeds ranging from 23.9 to 27.8 mm/min were obtained. The results revealed that when the flame-front speed increased from 23.9 to 27.7 mm/min, sinter productivity increased from 34.1 to 38.6 t/m2 d at relatively unchanged sinter strength. At higher moisture and flame front speeds, while productivity and TI both deteriorated, suggesting the optimum moisture and flame- front speed for the blend has been past. Similarly, with increasing flame-front speed sinter size distri- bution, as indicated by the Sauter mean size, initially improved but deteriorated as flame-front speed increased further to 27.8 mm/min. Mineralogy studie