机制砂混凝土抗拉性能试验研究.docVIP

PAGE  PAGE 5 机制砂混凝土抗拉性能试验研究 　　摘要：为研究不同龄期和不同替代砂率下机制砂混凝土劈裂抗拉强度的变化规律，在水泥用量保持不变的情况下，制作试件时改变机制砂对天然砂的取代率（0，25%，50%，75%，100%）。试验结果表明，劈裂抗拉强度值机制砂混凝土大于天然砂混凝土，随着机制砂替代率的提高，相应混凝土的劈裂抗拉强度逐渐增大，替代率为50%的劈裂抗拉强度比替代率为75%的劈裂抗拉强度大，稍小于替代率为50%的劈裂抗拉强度，说明该机制砂对天然砂的最佳替代率为50%左右。 　　Abstract： In order to study the change rules of split strength of the manufactured sand concrete at different replacement， concrete sample was prepared at the same cement consumption with the replacement ratios of manufactured sand by mass to the natural sand were respectively 0， 25%， 50%， 75% and 100%. The split strength of manufactured sand concrete was stronger than that of natural sand， and it showed an increasing trend with the increasing of replacement rate and age but the split of replacement rate of 50% was larger than the split of replacement rate of 75% and was slightly smaller than the split of replacement rate of 100%. This showed that the optimum re-placement ratio of the manufactured sand by mass to the natural sand was 50%. 　　关键词：机制砂；混凝土；劈裂抗拉强度 　　Key words： manufactured sand；concrete；splitting tensile strength 　　中图分类号：TU52 文献标识码：A 文章编号：1006-4311（2016）18-0080-03 　　0 引言 　　新建广通至大理铁路复线是泛亚铁路、滇藏铁路组成部分，正线全长175公里，旅客列车设计行车速度为200公里/小时。随着我国多年的大规模基础建设，不少地区河砂资源日趋正趋枯竭，在河砂资源较匮乏的云南、贵州等地更是如此，所以本工程铁路线下工程中桥墩采用机制砂为骨料的混凝土。机制砂混凝土的劈裂抗拉强度是混凝土的一项重要力学性能指标，其对混凝土的耐久性有重要的影响[1-2]，研究机制砂混凝土的劈裂抗拉强度对机制砂在该项目中的应用起着重要的决定作用。 　　1 试件制作与试验方法 　　试验的目的是通过对比天然砂、不同石粉含量机制砂与原状机制砂混凝土，研究机制砂与天然砂对混凝土劈裂抗拉强度的影响，找出机制砂混凝土劈裂抗拉强度随龄期和替代率变化的规律。 　　1.1 试件制作 　　水泥采用鑫鼎P?O42.5级普通硅酸盐水泥，机制砂采用石灰岩机制砂，具体参数见表1，减水剂采用聚羧酸高效减水剂（减水效果30%）。 　　本次试验采用边长为150mm的立方体标准试块，各试块的机制砂替代率分别为0，25%，50%，75%，100%，试块龄期分别为28d、60d、90d、120d、180d。 　　1.2 抗拉强度试验方法 　　混凝土轴心受拉试验的试件可采用在两端预埋钢筋的混凝土棱柱体。试验时用试验机的夹具夹紧试件两端外伸的钢筋施加拉力，破坏时试件在没有钢筋的中部截面被拉断，其平均拉应力即为混凝土的轴心抗拉强度。但用此种方法测定混凝土的轴心抗拉强度时，保持试件轴心受拉是很重要的，也是不容易完全做到的。因为混凝土内部结构不均匀，钢筋的预埋和试件的安装都难以对中，而偏心又对混凝土抗拉强度测试有很大的干扰，因此，目前国内外常采用立方体或圆柱体的劈裂试验来测定混凝土的轴心抗拉强度[3]。 　　本次劈裂抗拉强度试验按《普通混凝土力学性能试验方法标准（GB/T 50081-2002）》进行，如图1所示。试验时，在劈裂钢垫条和试块之间，应加一层三合板垫层，木垫条宽20mm，