环保型竹基酚化液基酚醛树脂胶粘剂的制备 化学专业学位论文.docVIP

黄山学院化学系优秀本科毕业论文 黄山学院化学系优秀本科毕业论文 环保型竹基酚化液基酚醛树脂胶粘剂的制备 [摘要] 本文深入探讨了酚醛比、催化剂的用量、终点粘度对环保竹基酚化液基酚醛树脂胶粘剂（BPF）性能的影响。实验结果表明，甲醛分2次加入，第一次加入总量的80%，催化剂1次加入，反应的保温温度为90℃，反应的终点倒泡粘度控制为4.0-5.0s，催化剂用量为17.5%（按酚化液的质量百分数计算）、醛酚比为1.9:1（甲醛与酚化液的物质的量之比）时，制备的BPF具有更低的游离甲醛、游离苯酚和优异的胶合性能。 [关键词] 竹基酚化液，酚醛胶，低游离甲醛，低游离苯酚 Environmentally friendly bamboo phenol of liquid-based phenolic resin adhesive [Abstract] This article discusses the effects of phenol formaldehyde ratio, amount of catalyst, the end viscosity on the performance of bamboo-based phenolic resin-based adhesive (BPF). The results showed that Results showed that the optimal experimental conditions was obtained as follow: adding formaldehyde 2 times; the reaction temperature ,90 ℃, the terminal bubble viscosity ,4.0-5.0s; catalyst 17.5 % (by weight of liquefied solution), formaldehyde phenol ratio of 1.9:1 (molar ratio)。The resultant BPF has a lower free formaldehyde, phenol and excellent glue performance as well. [Keywords] bamboo-based liquefied solution，PF adhesive，low free formaldehyde，low free phenol 前 言 传统的酚醛树脂胶粘剂（PF）因具有优异的胶接强度、良好的耐水性、耐热性及化学稳定性，是目前室外用人造板的主要用胶。近几年由于石油储量的减少和油价的不断上涨，以石油为原料的PF熟知的生产成本不断被提高；另外，在生产酚醛树脂过程中产生有毒游离苯酚和游离甲醛很难被除去，使得酚醛树脂的环保问题一直受到使用者的关注[1-4]。因此，研究低毒、低游离甲醛和低成本的酚醛树脂胶粘剂近年来成为胶粘剂领域的研究热点[5-6]。 在之前的研究中，我们初步确立竹基材料高值转化技术[7-8]：即采用选择性液化技术，对竹材特别是竹材剩余物（下脚料）竹粉进行液化，获得具有优良流动性能和贮存稳定性的竹基酚化液，用于制备具有环境友好竹基酚醛树脂胶粘剂；同时，通过特定的分离技术获得可高值利用的竹纤维素微粉（BCMP，bamboo cellulose micro-powder）。在以上研究和木质素基酚醛树脂胶粘剂（LPF）的研究基础上[9-10]，本文继续优化确定竹基材料的液化工艺，探讨采用竹基酚化液制备低游离醛和游离酚的竹基酚化液基酚醛树脂胶粘剂（BPF），并考察其胶合性能。 1 实验部分 1.1 原料、试剂与仪器 表1 实验主要仪器和试剂 名称型号生产厂家恒速搅拌器S212上海申顺生物科技有限公司电热套ZNHW巩义市英峪予华仪器厂电子天平ELB2000日本岛津电子分析天平BS110S北京赛多利斯天平有限公司磁力加热搅拌器DF-Ⅱ江苏省金坛市医疗仪器厂恒温水槽HK-1D南京大学应用物理研究所竹粉过10目筛网黄山金竹人造板厂苯酚A.R.国药集团化学试剂有限公司乙醇C.P.黄山酒厂盐酸A.R.国药集团化学试剂有限公司氢氧化钠A.R.国药集团化学试剂有限公司1.2 酚化液制备 将一定量的苯酚，加入置于装有搅拌器、冷凝装置、热电偶的四颈烧瓶中，加入竹粉与催化剂（盐酸），用电热套加热，控制温度在100-105℃之间，反应时间10-120min，之后将酚化液冷却至60-80℃，趁热抽滤，得竹材酚化液。 1.3 BPF的制备 将一定质量的竹材酚化液和质量分数为30%的氢氧化钠溶液，加入装有搅拌器、冷凝装置、热电偶的四颈烧瓶中