附录三常用金属材料性能介绍.doc

X PAGE 4/ NUMPAGES 5 X PAGE 5/ NUMPAGES 5 附錄三 常用金屬材料性能介紹 表一. 黃銅, 鈦銅, 磷青銅性能比較 定義7-3黃銅 70% Cu黃黃銅 65% Cu鈦銅磷青銅 6%Sn彈簧用 磷青銅銅編號C2600C2680TiCuR1C5191C5210化學成份?(%)Cu 70 Zn 30Cu 65 Zn 35Ti 3.1 Cu+Ti 99.5%minSn 6 P 0.2 Cu+Sn+P 99.7minSn 8 P 0.2 Cu+Sn+P 99.7min物理性質? 比重????(g/cm3) 熔點范圍??(?C ) 熱膨脹系數 (10-6/ ?C) 彈性系數 (kgf/mm2) 導電性??(%IACS) 8.53 915-955 19.9 (20-300 ?C) 11,200 28 8.47 903-930 20.3 (20-300 ?C) 10,500 27 8.70 1,040-1,070 18.6 (30-450 ?C) 13,000 13 8.83 890-1,045 17.6 (20-300 ?C) 11,200 14 8.80 860-1,025 17.6 (20-300 ?C) 11,200 13機械性質??回火 ??????0 1/4H 抗拉強度 1/2H (kgf/mm2) H EH SH 30-39 33-42 36-45 42-55 53min  30-39 33-42 36-45 42-55 53min  80min 95min  32min 40-52 50-62 60-70 65min  48-62 60-72 70-80 75-85???????0 1/4H 伸長率(%) 1/2H H EH SH40min 35min 28min - - 40min 35min 28min - -  15min 5min 42min 35min 20min 8min 5min  27min 20min 11min 9min???????0 1/4H 維克式硬度?1/2H (Hv) H EH SH 75-125 85-145 105-175 145min  75-125 85-145 105-175 145min  250-300 300-350  100-160 150-205 180-230 200min  140-205 185-235 210-260 230-270???????0 彈簧的??1/4H(M) 彈性極限?1/2H (KbO-1) H (kgf/mm2) EH(M) SH- - - - - - - - - -  70min 85min   25min 40min 47min 52min應力松馳XX@??????材料 錫?? ????暴露於蒸氯中O ?O ?O ?O ?O ????鹽霧實驗 腐蝕???暴露至二硫化?????物氯體中X X ? OO OO O應力蝕裂性XX?@@軟化溫度? (HV 80%)325?C (30min)325?C (30min)530?C (60min)360?C (60min)370?C (60min)生產范圍 厚度?mm 寬度 mm 卷料重量 kg/mm 0.04-3.0 6-610 0.5-3.5 0.04-3.0 6-610 0.5-3.5 0.06-0.8 6-400 0.5-2.0 0.05-2.0 6-610 0.5-35 0.05-2.0 6-610 0.5-35可用形狀 用途板材料帶,可用於汽車水箱, 連接器接頭及電燈裝置板材料帶,可用於汽車水箱, 扣子, 反射器板材料帶,可用於連接器, 開關, 繼電器及其他電子元件板材料帶 可用於端子, 連接器, 電子元件的彈簧及開關導線架, 膜盒及墊片Note: @ : excellent O : good ? : average X : not good 表二, 鈹銅性能介紹: 定義Brush Alloy 25 鈹銅合金Brush Alloy 165 鈹銅合金