甲基丙烯酸甲酯本体聚合反应的研究.doc

甲基丙烯酸甲酯本体聚合反应的研究 王宏叶 应化1003班 （西南科技大学材料科学与工程学院，绵阳621000） 摘要 本体聚合是制备有机玻璃等聚甲基丙烯酸甲酷(P M M A )制品的主要方法。本文主要介绍了现有对聚甲基苯烯酸甲酯本体聚合的一些研究方向，包括超声辐照下甲基苯烯酸甲酯的本体聚合、等离子体引发聚合甲基苯烯酸甲酯以及激光诱导甲基苯烯酸甲酯本体聚合，并对甲基苯烯酸甲酯本体聚合中存在的问题进行简要说明。 关键词 甲基苯烯酸甲酯 本体聚合 自由基链式聚合 自动加速 Research of Methyl Methacrylate (MMA) bulk polymerization reaction Hongye WANG (School of material science and engineering, the southwest science and technology university, mianyang, Sichuan; 621000) Abstract Bulk polymerization is the preparation of poly (methyl methacrylate products such as organic glass of the main methods.This article mainly introduced the existing of bulk polymerization of methyl methyl benzene acid some research direction, including under ultrasound irradiation bulk polymerization of methyl benzene acid methyl ester, plasma polymerization of methyl benzene acid methyl ester and laser induced bulk polymerization of methyl methyl benzene acid.And the methyl benzene acid methyl ester briefly explain the problems existing in the bulk polymerization Key words methyl benzene acid methyl ester; bulk polymerization; Free radical chain polymerization; Automatic acceleration 1 引言 PMMA俗称有机玻璃，是一种开发较早的重要热塑性塑料，具有较好的透明性、化学稳定性和耐候性，易染色，易加工，外观优美，在建筑业中有着广泛的应用。有机玻璃通常采用甲基丙烯酸甲酯(MMA)本体聚合方法制备。 甲基丙烯酸甲酯在过氧化苯甲酰引发剂存在下进行自由基聚合反应。自由基加聚的工艺方法主要有四种：本体聚合、溶液聚合、悬浮聚合及乳液聚合。本体聚合由于反应组成少，只是单体或单体加引发剂，所以产物较纯，但散热难控制；溶液聚合过程易控制，散热较快，不过产物中含溶剂（有些污染环境），后处理比较困难；悬浮聚合以水作溶剂，水无污染，散热好，易除去，但要求单体不溶于水，故在应用上受限制；乳液聚合反应机理不同，可以同时提高聚合速度聚合度，散热好，易操作【1】。 甲基丙烯酸甲酯在BPO引发下自由基聚合： 自由基聚合属连锁反应，一般有三个基元反应：链引发，链增长，链终止（有时还会出现链转移）反应。 链引发： R· +MM→RM· 链增长： RM· +M→RMM· +M→RMMMM· +M →…→﹋M· 链终止： ﹋M·+ ﹋M·→‘死’聚合物 本体聚合是不加溶剂或其他介质，只有单体本身在引发剂、热、光、辐射的作用下进行的聚合【2】。本体聚合的特点是产物纯净，可不进行纯化后处理，适于生产浅色透明的板材和型材，但当反应到一定程度时粘度增大，大分子链自由基活性降低，阻碍了链自由基的相互结合，使链终止速率减慢，而小分子单体却依然可以自由与链结合，链增长速率不会受到影响，从而导致自动加速效应，即聚合速度随单体转化率增大而急剧增加的现象，内部温度急剧上升，又继续加剧反应，如此循环，而粘度又屏蔽热量，使局部温度过高，严重影响聚合物的性质。【3】同时本体聚合体系粘度大，散热非常困难，散热不良轻则造成局部过热，使聚合物分子量分布变宽，降低产品的机械强度，重则引发爆聚导致产品报废。本文将对目前甲基丙烯酸甲酯本体聚合的方法和主要工艺进行综述