Process parameters matching pairs of dental Ti.doc

 PAGE \* MERGEFORMAT 6 Process parameters matching pairs of dental Ti Author: Gao Bo, Yan Xiaodong, Wang Zhongyi, Chen Jing [Keywords:] microstructure Influence of technologic parameter matching on laser solid forming properties of TiZr alloy for oral prosthesis [Abstract] AIM: To find relatively proper technologic parameter matching by evaluating its influence on laser solid forming properties of TiZr alloy powder. METHODS: Single cladding test under different technologic parameter matching was carried out by orthogonal design method and the single cladding height (H ) and the single cladding width (W) were measured to find the suitable technologic parameter matching. The microstructure of TiZr alloy formed under this suitable technologic parameter matching was analyzed by scanning electron microscope (SEM). RESULTS: When the ratio of laser power to facular diameter was 2.7 kW / 3 mm, the powder feeding speed was 90 r / min and the moving speed of numerical control machine was 5 mm / s, better H (826.61 μ m) and W (3504.61 μ m) were obtained. The SEM photograph showed that directional solidification cladding layer with thin and dense columnar dendrites was acquired. CONCLUSION: Under proper technological control, dental TiZr alloy powder is a new material for laser solid forming. [Keywords] laser forming; TiZr alloy; microstructure [Abstract] Objective: To study the titanium-zirconium (TiZr) alloy powder during laser solid forming process parameters on formability of the impact of compare match to explore the forming process parameters. Methods: Orthogonal design of statistical methods to test group, respectively, a combination of different process parameters under TiZr powder cladding of single-storey single-channel experiments to measure the single-clad height (H) and single-channel cladding width (W), and then optimize the process parameters for multi - accumulation was observed after forming TiZr alloy. Results: In the laser power and spot diameter r