20Mn2,GBT3077-199920Mn2steel,20Mn2stainlesssteel.docVIP

GB 20Mn2 steel20Mn2 steel has medium strength. The coldstraining plasticity of 20Mn2 steel is high, low temperature property is good, weldability and machinability are passable. And compared with carbon steel with corresponding carbon content, the quench-hardening ability of 20Mn2 steel is higher. In oil the critical full hardening diameters are 4-15mm. But in heat treatment 20Mn2 steel has the tendency of overheating, decarburization sensitivity and temper brittleness. This kind of steel has an appropriate quench-hardening ability, after the suitable metal heat treatment, the microstructure of the body is the uniform sorbite ,bainite or superfine pearlite, thus it has the high tensile strength.GB 20Mn2 steel’s application20Mn2 steel is mainly used for making the carburized parts which don’t have high demand on surface and section size 50 mm in diameter, such as carburized small gear, small axis, low requirements piston pins, cross pin head, diesel engine sleeve, valve plunger mandril, gearbox joystick, steel bushing, etc of automobiles, tractors and in machine tools production. In addition, in the hot rolling and normalizing state 20Mn2 steel can also be used for manufacturing rivet welding parts, screw and nut etc.GB 20Mn2 steel’s equivalent material in different standard. JIS G4106 ASTM A29M AISI SAE EN 10028-2 ISO 683-1 BS 970 Part 3 ГOCT GB/T3077-1999 SMn420 (SMn21) 1524 1024 1524-1024 P355GH 22Mn6 150M19 20Г2 20Mn2 GB 20Mn2 steel’s chemical composition C Si Mn Cr Ni Cu P S ≤ ≤ ≤ ≤ 0.17～0.24 0.17～0.37 1.40～1.80 0.30 0.30 0.25 0.035 GB 20Mn2 steel’s mechanical property Tensile Strength（σb/MPa） Yield point（σs/MPa） Elongation（δ5/%） Reduction of Area（ψ/%） Impact Absorbing Energy（Aku2/J） Brinell Hardness（HBS100/3000） Annealing or High Tempering ≥785 ≥590 ≥10 ≥40 ≥47 ≤187 Henan Bebon Internationl Co., Ltd is specialized in offering every kind of structural alloy steel plates.Bebon International is a professional 20Mn2 steel exporter