CASEHARDENINGSTEELAISI8620-STStainless.pdfVIP

CASE HARDENING STEEL–AISI 8620 AISI 8620 Nickel–Chrome–Moly TYPICAL CHEMICAL ANALYSIS Carbon 0.20% Carburising Steel, generally supplied Silicon 0.25% as rolled to HB 255max. Carburised and heat treated it develops a hard Manganese 0.80% Chromium 0.50% wear resistant case to HRC 60-63 and Nickel 0.55% a tough strong core with a typical Molybdenum 0.20% tensile strength range of 700-1100 MPa, in small to medium sized sections. RELATED SPECIFICATIONS: AS 1444-1996 8620 or 8620H TYPICAL APPLICATIONS: Arbors, pinions, bushes, camshafts, kingpins, EN10084-1998 1.6523 20NiCrMo2-2 or 1.6523H20NiCrMo2-2H ratchets, gears, splined shafts etc. Or can be used for high tensile applications uncarburised but JIS G 4103 SNCM 220 or through hardened and tempered. JIS G 4052 SNCM 220H UNS G86200 or H86200 . Through hardening properties fair with good toughness due to the low carbon and medium alloy content, also suitable for Nitriding. TYPICAL MECHANICAL PROPERTIES – Quenched and Tempered at 200°C Section Yield Strength Tensile Strength Elongation Impact Izod Hardness mm MPa