海洋环境钢筋混凝土桥梁腐蚀机理及防腐措施_赵本栋.pdfVIP

DOI:10.14018/j.cnki.cn13-1085/n.2014.09.043 Value Engineering ·87 · 海洋环境钢筋混凝土桥梁腐蚀机理及防腐措施 Study on Corrosion Mechanism and Anti-corrosion Protection of Reinforced Bridge in the Marine Environment 赵本栋① ZHAO Ben-dong ；林辉② LIN Hui ；邬晓光① WU Xiao-guang （①长安大学公路学院，西安710064 ；②宁德沈海复线宁连高速公路有限公司，宁德352100） （①School of Highway ，Changan University，Xian 710064 ，China； ②Ningde Shenhai Multiple Track Ninglian Highway Co. ，Ltd. ，Ningde 352100 ，China） 摘要： 海洋环境中的结构腐蚀包括混凝土和钢筋两方面，相互影响会产生严重的后果。为了减少或避免桥梁损伤，必须采取切实 可行的防腐措施。论文针对腐蚀因素，提出结构材料及设计施工等多方面的防腐措施。 Abstract: The corrosion of structure in the marine environment includes two aspects of concrete and reinforcement, whose mutual influence would have serious consequences. In order to reduce or avoid the bridge damage, viable anticorrosion measures must be taken. In view of the corrosion factors, the anticorrosion measures which refer to material, design and construction were put forward in this paper. 关键词： 腐蚀机理；防腐；海洋；钢筋混凝土 Key words: corrosion mechanism ；corrosion protection ；ocean ；reinforced concrete 中图分类号： 文献标识码： 文章编号： TU37 A 1006-4311 （2014）09-0087-02 0 引言 事实上，由于桥梁结构长期处于海洋环境中，未得到 从19 世纪20 年代发明水泥到今天，水泥混凝土的材 妥善防护的钢筋混凝土结构的劣化速度非常快，另外，跨 料和技术，经历了巨大的变化。从最初的普通强度发展到 海桥梁一旦发生损坏，在修复过程中一旦受到自然条件的 现在的高强度高性能混凝土，由于混凝土的材料性能的不 制约，就会显得十分困难，代价也是很昂贵的。因此，研究 断改善。使其具有取材广泛、施工方便、维护简单、成本较 海洋环境中桥梁结构的防腐问题对于维修既有跨海桥梁 低、耐热性能好等优点，使得钢筋混凝土逐渐成为了海洋 及提高新建跨海大桥耐久性是很有必要的。 环境下桥梁建设的首选形式。 1 混凝土腐蚀机理 —————————————————————— 海水环境中的混凝土腐蚀主要受多组分的侵蚀性离