铝合金导轨的铸造工艺.pdfVIP

学兔兔 Feb．2010 VOI．59 N0．2 ·197· ， -～ ^_ ^^ _^ ^^ {经验交流 ； 、^ ’r 、 0_‘，’ ■ ’n● _ 铝合金导轨的铸造工艺 孔繁钢 (内蒙一机集团能达专用设备有限责任公司，内蒙古包头014032) 摘要：铝合金导轨长度长、壁厚薄且不均匀，铸件的技术及质量要求较高，给导轨铸件的生产带来了较大的难度。通 过对导轨的铸件结构进行充分的分析，制定了合理的铸造工艺，对主要部位采取了相应的工艺措施，严格控制熔炼及 浇注操作，经过多次试制，完成了导轨铸件的生产试制任务，经加工检验符合零件的使用要求，为铸件批量生产奠定 了基础。 关键词：铝合金；导轨；铸造工艺 中图分类号：TG292 文献标识码：B 文章编号：1001—4977(2010)02—0197—03 Casting Technique of Aluminium Alloy Slide Way KONG Fan—gang (Special Equipment Co．，Ltd．of Inner Mongolia First Machinery Group Corporation，Baotou 014032， Inner Mongolia，China) Abstract：it iS difficult to produce Al alloy slide way for its Iong length。uneven wall thickness and higher quality requirements．A reasonable casting process was established through SM仟icient analysis on the structure of the slide way casting，some measures were taken to the key pads of the casting and the melting and casting operation were strictly controlled．through a series of trial production，finally the qualified casting was obtained，which iS in Iine with the requirements for the production of slide ways．This establishes a foundation for mass production of the castings． Key WOrds：aluminium alloy；slide way；casting technique 铝合金导轨是某产品上重要的零件之一。导轨铸 件的技术要求及质量要求较高，铸件的许多部位均要 求进行探伤检查，不能有任何铸造缺陷，导轨滑行面 及支耳等部位的内部组织要求致密等，这些要求大大 增加了导轨铸件的生产难度。我们通过对铸件结构及 技术条件进行充分地分析后认为：该铸件属于细长箱 图1 导轨铸件 体类铸件，内部许多筋板相交形成了多处热节，易形 Fig．1 Slide way