学兔兔 第26卷第5期 粉末冶金技术 Vo1．26．No．5 2008年10月 Powder Metallurgy Technology Oct．2008 TiO2片状粉末的溶胶一凝胶法制备 李 悦 叶红齐 刘 辉 (中南大学化学化工学院粉体技术研究所，长沙410083) 摘 要： 以玻璃为基片先涂覆一层脱模层，再以溶胶一凝胶涂膜法在其表面涂覆Ti02薄膜，经丙酮浸泡后 得到片状粉末。试验考察了影响溶胶形成及最后片状粉末形貌的一些因素。XRD及SEM结果表明，片状粉 末于400*(2煅烧3h后为锐钛矿型，具有明显片状结构，粒径小于60tim，厚度约为Ittm。 关键词：片状Ti02；溶胶一凝胶法；脱模层 Preparation of flaky TiO2 powders by a novel method Li Yue，Ye Hongqi，Liu Hui (Institute of Powder Technology．College of Chemistry and Chemical Engineering， Central South University，Changsha 410083，China) Abstract：The flat glass substrates were precoated with a resin releasing agent，then coated with Ti02 by sol—gel method．The flaky powder was obtained by immersing the coat in acetone．Some factors effecting the formation of sol and morphology of flake powder were discussed．The XRD and SEM results showe that flake TiCh powder calcined at 400*(2 is composed of anatase type phase with a size below 6OⅡm，and thickness of about lpm． Key words：flaky Ti02；sol—gel method；releasing coat 近年来，为适应电子材料、生物工程材料、复合 小、单分散性好，但工艺复杂、能耗大，成本高，不能 材料的需求，片状粉体材料得到了较快的发展。因 制造有效量的产品；液相法具有合成温度低、工艺简 其特殊的二维平面结构，在化学性能上表面活性适 单、能耗少以及设备投资小的优点。溶胶一凝胶法 中，既能与其它活性基团有效结合，又不易团聚而便 是液相法中的一种重要方法，是目前实验室和工业 于有效分散；有足够的强度和稳定性，具有良好的附