材料学基础13.pptVIP

材料科学基础Fundamental of Materials 3. Application of Schmid’s law Solution: Draw a orientation cell. Label the loading direction in the cell. Determine the active S.S. by reflection rule. Label the loading direction in standard projection. case1. along FCC, orientation triangle : slip system is Determine the active slip systems by Reflection Rule. ④ locate inside the orientation triangle ( ), single slip. locate at the edge of the orientation triangle ( ), double (duplex) slip. locate at the corner of the orientation triangle, multiple slip. A tensile force is applied on a BCC cylindrical bar with across section of 25mm2. The initial axis is . The CRSS is 0.4MPa . The slip plane is . §4.3 Change in Reference Direction Reference Places during Slip From the figure Examples: [given] [ ask ] [solve] Discussion: for compression if located on S.P. then and Ⅱ.Change of reference planes take two vectors in the reference plane. let after slip Examples and Discussions All directions which lie on slip plane do not change after slip. Slip plane remains unchanged after slip. if on slip plane then Exercise * * Prof: Tian Min Bo Tel: E-mail: tmb@mail.tsinghua.edu.cn Department of Material Science and Engineering Tsinghua University. Beijing 100084 Lesson thirteen How to determine the active S.S. for all the equivalent S.S. Determine the active S.S. by Reflection Rule. Orientation cell for cubic crystals. Given: BCC Crystal having {110}111slip system. Determine : active slip system in response to tensile loading along Determine the active slip systems by Schmidts law Draw a standard projection x=z line x=y line y=z line Mirror rule case2. along orientation trian