掺锂渣再生粗骨料混凝土抗压强度试验研究.pdfVIP

学兔兔 2015年第8期 混凝土与水泥制 品 2015 No．8 8月 CHINA CONCRE IE AND CEMENT PR0DUCTS August 掺锂渣再生粗骨料混凝土抗压强度试验研究 于 江，严文龙，秦拥军，罗 玲 (新疆大学建筑工程学院，乌鲁木齐830047) 摘 要：锂渣及再生粗骨料对混凝土抗压强度有一定的影响，通过轴心抗压试验获得了立方体与棱柱体抗压强 度之间的线性关系。结果表明，适量的再生粗骨料和锂渣可以有效提高混凝土28d抗压强度，当再生粗骨料取代率 为30％，锂渣掺量为20％时，28d的立方体和棱柱体抗压强度最大，较同龄期下未掺锂渣的普通混凝土增长了39．1％ 和48．2％。 关键词：锂渣；再生粗骨料；立方体抗压强度；棱柱体抗压强度 Abstract：Lithium stag and recycled coarse aggregates have a certain influence on the compressive strength of con— crete，thmu【gh the axial compressive test，the linear relationship of compressive strength between the cube and prism were obtained．rrhe results show that the right amount of recycled coarse aggregate and lithium slag can effectively improve the 28d compressive strength．When the replacement rate of recycled coarse aggregate is 30％ and the lithium slag content is 20％，the 28d compressive strength of cube and prism is the largest，is increased b．y 39．1％ and 48．2％than the compres— sive strength of the ordinary concrete which is not added by lithium slag in the same age period． Key words：Lithium slag；Recycled coarse aggregate；Compressive strength of cube；Compressive strength of prism 中图分类号：TU528．041 文献标识码：A 文章编号：1000—4637(2015)08—94一O5 0 前言 力学性能有一定的提高作用[5-6]。但目前国内外尚无 目前，国内外已对再生粗骨料混凝土的抗压性 对掺锂渣再生粗骨料混凝土这种新型结构材料进 能进行了大量研究。再生粗骨料自身的缺陷造成其 行系统的探索。 强度不高【 ，一定程度上限制了再生粗骨料混凝土 基于再生粗骨料混凝土的研究现状及新疆地 的推广和应用。为了弥补其在强度上的不足．将锂 区特点，本文通过测定立方体及棱柱体的抗压强度 渣作为掺合料加人混凝土中，以期改善混凝土的抗 来分析影响掺锂渣再生粗骨料混凝土抗