某工程管道腐蚀原因及处理方法的探讨.pdfVIP

学兔兔 江苏建筑 2013年增刊(总第 158期) 某工程管道腐蚀原因及处理方法的探讨 姚立军 (江苏省建筑设计研究院有限公司。江苏南京 210019) [摘 要】 某工程运行4年多，检查发现热水管道腐蚀、结垢情况严重。经定性分析，认为管材和热交换器自身材质、两种 材质的管道连接处理、管道焊接处引起缝隙腐蚀、水中溶解氧等几方面是造成管道腐蚀、结垢的主要原因。针对上述原因。采 取更换管材、更换热交换器、增设全程水处理器的处理方法，解决管道腐蚀和结垢问题，改造后运行一年多时间，情况良好。 【关键词] 热水管道；腐蚀；结垢；处理方法 [中图分类号】TU991．38 [文献标识码]A 【文章编号]1005—6270(2013}so一0099—02 To Investigate the Corrosion Reason and Processing Method of Pipeline YAO Li-jan Oiangsu Province Architectural DesignResearch Institute Co．，Ltd，N ing Jiangsu 210019 China) Abstract：A project had runned for more than 4 years，inspection found that hot water pipelines were cor— rosed and sealed seriously．Through qualitative analysis，the major causes of pipeline corrosion and scaling are the materials of pipeline and heat exchanger，two kinds of connection processing，the crevice corrosion of pipeline welding，dissolved oxygen and other aspects．For the above reasons，processing method of solving the problem of pipeline corrosion and scaling is replacing pipeline and heat exchanger and adding the water pro— cessor．It is running fine more than one year with these renovation． Key words：hot water pipe；corrosion；sealing；processing method 1 工程概况 本工程为南京某多层综合楼。由3栋建筑组成．总建筑 面积约3万 m2。地上4层，地下 l层，于2005年8月完成 施工图设计，同年 1O月开工建设，并于2007年5月正式投 ● 入使用。原设计冷热水管材均为不锈钢管材，施工时建筑物 内部实际采用内衬不锈钢复合钢管．管径小于 100 mm采 用丝接。管径大于等于100 mm采用卡箍连接：室外管沟内 冷热水主管道采用不锈钢管道。卡箍连接。 2 腐蚀情况 一 口 2．1管道腐蚀 图1部分热水管道腐蚀情况 工程运行4年多时间．期间使用方反映生活热水系统 换器．主体材质为碳钢．使用方定期清洗时发现热交换器内 的水质很差．使用单元卫生间器具放水时出现大量黄水和 壁腐蚀现象非常严重．在热交