应用热场分析避免砂芯烧结缺陷.pdfVIP

学兔兔 应用热场分析避免砂芯烧结缺陷 汪大新，高 华，李 杰，牛德良 (合肥铸锻厂，安徽 合肥 230601) 摘要：分析了铸件浇注与凝固过程中易烧结部位的热场分布，确定了不同工艺条件下配重件的 良性热场和不良热场，探讨了砂芯烧结缺陷形成的主要原因。在V法铸造工艺设计中采取相应 的Z-艺措施和积极的工艺干预以消除对热场分布的不良影响，获取了健全的铸件 对同一种铸 件几个工艺方案的对比，说明热场分析方法在V法铸造生产中的实用价值。 关键词：铸造工艺；砂芯烧结；热场 中图分类号：TG249．9 文献标识码：A 文章编号：1 673-3320(2014)05—0018-03 Using Thermal Field Analysis to Avoid Core Sintering WANG Daxin，GAO Hua，LI Jie，NIU Deliang (Hefei Casting and Forging Factory，Hefei 230601，Anhui，China) Abstract：The distribution of thermal field for the parts sintered easily in pouring and soliditication process of casting was analyzed．the optimum and harmful thermal field of counter weight castings was determined at different process conditions，and the main causes of sand core sintering defects were discussed．Using the corresponding process measures in V-process design，the bad influence of therm al field was eliminated to obtain a sound casting．The comparison of several process schemes shows that the analysis of therm al field has practical value in V-process． Key words：casting process；core sintering；therm al field ~lJ2012年，近90％的工程车辆配重都来自于 艺干预，采取适合的铸造工艺布置，以避免产品 V法铸造生产。大部分配重为厚大铸件，热容量 中铸造缺陷的产生。 大。这类铸件中砂芯相对铸件的体积比小，砂芯 1 工艺分析 受铁液包裹时间长，发生铁液向砂芯渗透的概率 较大，经常出现严重的砂芯烧结现象，导致清铲 配重铸件属大吨位厚大件，其外形结构如 图1所示。铸件装配孔砂芯周围属于铁液富集区 困难，影响铸件尺寸精度、表面质量及生产效 域，经常出现砂芯烧结的现象。 率。也就是说铸件砂芯部位的局部过热引起了缺 陷。 在金属液全部浇入型腔后至金属液凝固的 这段时间里，型腔内金属液 (包括铸件和浇冒系 统)以温度为表征的比内能 (单位质点含有的能 量，J／kg)分布即为热场…。本文通过对浇注完毕 后型内金属液总体的温度分布，以及随冷却条件 的差异导致温度分布变化的研究