耐火砖成型模板的失效分析与选材.pdfVIP

维普资讯 学兔兔 Feb．2008 铸 造 V01．57 N0．2 FO RY 耐火砖成型模板的失效分析与选材 陈 丹 (辽宁科技学院，辽宁本溪117022) 摘要：分析了1o钢制耐火砖成型模板过早失效的形式从原因，论证了采用稀土镁球铁代替1o钢制作成型模板的可行 性。生产实践表明，稀土镁球铁模板的使用寿命是1O钢的1． 2．0倍，且可降低成本，节约能源。 关键词：稀土镁球铁；模板；失效；选材 中图分类号：TG255 文献标识码：B 文章编号：1001—4977(2008)02—0167—03 Failure Analysis of FOrming Dies for Firebrick and Selection Of Its MateriaI CHEN Dan (Liaoning Science and Technology College，Benxi 1 1 7022，Liaoning，China) Abstract：The premature failure modes of firebrick form ing dies made of steeI 1 0 and jts failure reason are analyzed．The possibility of using rare earth Mg ductile iron to replace steel 1 0 was expounded．Production practice showed that the service Iife of the rare earth Mg ductile jroB dies jS 1．6．2．0 times as long as that of steeI 1 0．And using the rare earth Mg ductlie jron could Iower the cost and save energy resources． ’ Key WOrds：rare earth Mg ductile iron；forming dies；failure；material selection 耐火砖成型模板工作面大，在200 t压力机上承受 中前后左右侧面四块模板所受磨损最为严重，失效较 着耐火材料坚硬颗粒的挤压、刮削和研磨，其服役条 早。一般每套模具约冲压2 000～4 000块耐火砖即告失 件较为恶劣。因此要求模具工作面具有高硬度、高耐 效。 型模板简图如图1所示。模板失效形式多种多 磨性、足够的强度和适当的韧性。国外有使用高合金 样，除了操作以及安装不当而失效外，下列几种失效 冷作模具钢制作模板，热处理后表面硬度高、耐磨性 形式较多见。 好，但脆性大，模具安装时易开裂，且成本高。国内 不少耐火材料厂曾试用高铬铸铁、高碳铬钼耐磨合金 以及硬质合金等，或对碳钢制模具进行渗硼表面强化， 或渗碳与硼氮共渗复合处理等Il-4]。但由于种种原因未 得到广泛应用。 某厂选用lO钢制作模板，原采用980~Cx8 h高温固 体渗碳，后又改用930℃x15 h气体渗碳预冷到880℃ 后冰盐水淬火，经矫直后即可使用。材料成本低，机 加工及热处理比较简便，故应用较广。但