学兔兔 NOV．2012 VOI．61 NO．11 ·1361· 树脂和固化剂含量对自硬呋喃树脂砂 抗拉强度的影响 张集滕，李 瑞 (上海烟草机械新场铸造有限责任公司，上海201314) 摘要：研究了自硬呋喃树脂和磺酸固化剂的不同加入量对树脂砂抗拉强度的影响。结果表明：随着树脂加入量的增 加，树脂砂的初始强度 (1 h)、中间强度 (8 h)和终强度 (24 h)都呈现先增后减再增的趋势，当树脂加入量为 1．6％时，型砂的抗拉强度最高；随着固化剂加入量的增加，型砂的抗拉强度呈现先增后减的趋势，当固化剂含量为 树脂含量的50％a~，型砂抗拉强度出现峰值。 关键词：自硬呋喃树脂；磺酸固化剂；抗拉强度 中图分类号：TG221 ．1 文献标识码：A 文章编号：1001—4977(2012)1l一1361—02 Effects of Furan Resin and Hardener Contents on Tensile Strength of No．Bake Furan Resin Sand ZHANG Ji—teng，LI Rui (Shanghai Tobacco Machinery Xin Chang Foundry Co．，Ltd．，Shanghai 2013 14，China) Abstract：The ef-fects of the additions of the no—bake furan resin and sulphonic acid hardener on the tensile strength of resin sand were studied．The results show that with the increasing of the addition of the resin．the tensile strength including the initia1 strength (1 h)，middle strength(8 h) and final strength (24 h) all first increases，then decreases，and again increases，the tensile strength reaches the highest value when the furan resin content iS 1．6％：the tensile strength first increases．then decreases with the increasing of the hardener content． when the hardener content is 50wt．％ofthe resin．the tensile strength iS the highest． Key words：no—bake furan resin；sulphonic acid hardener；tensile strength 自硬呋喃树脂砂具有尺寸精度高、生产效率高、 砂温为25～30℃)，其总酸度为19．36％，游离硫酸为 溃散性好等优点，因此得到了广泛的研究及应用[】-4]。 1．22％。 目前，国外树脂加入量一般在2％以下，日本赤阪铁工 1．2 试验条件及强度测试方法 所新砂树脂加入量仅为1．1％，随着旧砂回用次数的增 在室温25～30℃，相对湿度为55％～60％ (6月)条 多，树脂加入量还可进一步降低No．7％l 5l。国内各铸造 件下进行试验。将一次回用砂、树脂及固化剂混制2 厂因技术水平，树脂及固化剂品质的不同，为了满足