超高伸长率硅烷封端聚醚密封胶的研制_曾军.pdfVIP

建筑密封 超高伸长率硅烷封端聚醚密封胶的研制 胡新嵩，曾辉文，崔少伟，龚建玲 曾 军， （广州市高士实业有限公司，广东 广州 510450） 摘要：以硅烷封端聚醚预聚物为基胶， 加入除水剂、交联剂、增塑剂、填料、偶联剂、催化剂等助剂，制备了一种超高伸长 率的单组分硅烷封端聚醚密封胶，并研究了增塑剂的类型、填料的用量、偶联剂的种类及预聚物的配比对密封胶性能的 影响。 关键词：密封胶；硅烷封端聚醚；高伸长率；增塑剂；填料；偶联剂；预聚物配比 文章编号：1007-497X （2015）－20－0020-04 中图分类号：TU502 ；TU57+8 文献标志码：A Development of High Elongation Silane-terminated Polyether Sealant Zeng Jun ，Hu Xinsong ，Zeng Huiwen ，Cui Shaowei，Gong Jianling （Guangzhou Glorystar Chemicals Co,. Ltd., Guangzhou, Guangdong 510450, China） Abstract: High elongation silane-terminated one component polyether sealant was prepared by silane-terminated polyether as the basic gel, water removal agent, cross linker, plasticizer, fillers, coupling agent, catalyst and other assisting agent. The influences of kinds of plasticizer, content of filler, kinds of coupling agent and ratio of prepolymer on properties of the sealant were studied. Key words: sealant; silane-terminated polyether; high elongation; plasticizer; filler; coupling agent; ratio of prepolymer DOI:10.15901/ki.1007-497x.2015.20.006 目前，建筑领域应用较多的弹性密封胶主要有3 易污染基材、表面涂饰性差等问题[1-4] 。硅烷封端聚醚 类：聚硫密封胶、硅酮密封胶和聚氨酯密封胶。这些 密封胶是一种新型密封胶，它结合了硅酮密封胶和聚 密封胶自身存在的一些缺陷或多或少地限制了其在 氨酯密封胶的优点，具有耐水、耐候，高弹性，粘结性 某些领域的应用：聚硫密封胶分子链中包含不稳定的 能优异，基材适应性广，不含游离—NCO 基团，表面 二硫键，因而长期耐久性和抗形变位移能力相对较 可涂饰，对基材无污染，低VOC ，环保等特点，应用范 差；聚氨酯密封胶对湿气十分敏感，贮存稳定性差，固 围更加广泛。本文以硅烷封端聚醚预聚物为基胶，加 化时易形成气泡，影响密封胶的力学性能，同时，聚氨 入除水剂、交联剂、增塑剂、填料、偶联剂、催化剂等助 酯密封胶对表面光滑的无孔基材进行粘结时，需使用 剂，制备了一种超高伸长率的单组分硅烷封端聚醚密 底涂；硅酮密封胶应用最为广泛，但也存在强度一般、 封胶。 —— ——————————— 1 实验部分 收稿日期：201