新型TiC钢结硬质合金致密化技术-中南大学学报.PDF

40 6 () Vol.40 No.6 2009 12 Journal of Central South University (Science and Technology) Dec. 2009 TiC ( 410083) Fe-3.0Cr-3.0Mo-0.5Cu-0.5C-33TiC TiC TiC TF125.3 A 1672−7207(2009)06−1563−05 Densification processing of a new steel bonded titanium carbide XIONG Yong-jun, LI Xi-bin, LIU Ru-tie, ZHAO Fu-an (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) Abstract: The Fe-3.0Cr-3.0Mo-0.5Cu-0.5C-33TiC mixed powders were prepared by high energy ball milling in a planetary ball mill. The sintered alloy was treated by HIP (hot isostatic pressing) and forging. The effect of ball milling time, HIP and forging on the microstructure, properties and porosity of alloy was studied. The results show that high energy ball milling refines and homogenizes the mixed powders, accelerates the sintering process, and with the increase of milling time, the grain is finer and the alloy is denser. HIP and forging is beneficial to decrease or remove the pole formed during the sinter course, and as the last process, forging breaks the junctions between TiC particles, the microstructure and mechanical properties of alloy are improved. Key words: steel bonded titanium carbide; densification; high energy ball milling; HIP (hot isostatic pressing); forging TiC TiC TiC TiC (HV 3 200) (3 150 ) TiC 20 60 TiC [5−