变形次数对LC4合金T5态组织性能的影响.pdfVIP

上半月出版 Casting. Forging. Welding号金属铸锻焊技术 变形次数对LC4 合金T5 态组织性能的影晌 韩保杰，张星，张治民 (中北大学精密成型中.~ J.，西太原 030051) 摘 要:以铝铸侯铜系变形 LC4 铝合金为研究对象，通过研究塑性变形次数对热挤压组织细化加时效处理后组织 性能的影响，改善了 LC4 合金的综合力争性能，以探索铝合金的强化方法，扩大铝合金的应用范围。 关键词:LC4 铝合金;变形次数;时效处理;组织;性能 中图分类号:TGI46.2 文献标识码:A 文章编号: 1001-3814(2011)19-0031-03 EfTect of Deformation Times on Microstructure and Properties of LC4 Alloy in T5 State HAN Baojie, ZHANG Xing, ZHANG Zhiming (丹ecision Forming Center, North University 01 China, r.ω严皿n 030051 , China) Abstract: Using aluminum and zinc magnesium alloy copper as the typical representative of defonnation LC4. By investigating the plastic deformation times of hot extrusion microstructure after thinning add aging treatment, the microstruc阳re of the LC4 alloy was improved. To explore the aluminum alloy s出ngthening methods , the application range of the aluminum alloy was expanded. Key words:aluminum LC4; defonnation times; aging treatment; microstructure; properties 铝加工工艺方法主要有.回归再时效和形变热处 变形处理:对于 LC4 铝合金，其大多数是过饱 理。虽然经过时效处理可显著提高硬度或强度，改善 和的固帘体，随锻造温度降低，从固溶体中析出强化 应力腐蚀敏感性IIi ，但同时也使合金的强度比时效峰 相， 300.C 时有较多的 S 相、T 相及其它相，导致合 状态有所降低，因此，不能充分发挥材料的性能潜力。 金工艺理性差。温度高于 450.C 时，原子振幅加大， 晶界及原子间结合力削弱，含金期性差[匀，鉴于此本 形变热处理可提高高强铝合金的强度，对铝合金形变 热处理的研究，多限于其最终性能Pl ，但对于含金在形 实验采用 350.C LC4 锤锻时允许变形程度不得超过 o 变热处理各工艺阶段的组织性能变化研究尚少凶。本 6鹏也，而在液斥机上锻造时，允许变形量 65%~85%阁。 文通过对形变热处理LC4 合金组织和性能的系统研