聚氨酯合成工艺.doc

200万米/年聚氨酯合成革厂的工艺设计 摘要 聚氨酯（PU））Abstract Polyurethane synthetic leather (PU) belongs to a class of polyurethane elastomer, the industrialized production method mainly has two kinds of dry and wet. Through the synthetic leather development history, performance, application market understanding of PU, determine the design process with an annual output of 2000000 meters of polyurethane synthetic leather. Mainly from the production formula, process design; further PU synthetic leather material balance in production and energy balance. In order to ，determine the parameters of polyurethane synthetic leather technology, production process and main equipment selection. At the same time also synthesis design leather waste treatment and safety technology production enterprise of polyurethane. Keywords：polyurethane?(PU) Synthetic leather dry process wet process集团范围 ??本标准规定了聚氨酯合成革的产品分类、要求、试验方法、检验规则及标志标签、包装、运输、储存适用于针刺非织造布经聚氨酯树脂湿法加工、溶剂萃取以及系列后整理工艺制成的具有中空藕状纤维结构的聚氨酯合成革。 产品分类 产品按用途分类，见表1。 用途 Ⅰ类 箱、包、带、家用革等 Ⅱ类 球类用革 Ⅲ类 鞋面用革 1.4.3 规格 （1）产品厚度、宽度偏差和长度偏差应符合表2要求。 厚度及偏差 宽度及偏差 每卷长度偏差 厚度 偏差 宽度 允许偏差 Ⅰ类 ≥1.10 ±0.10 ≥1300 ±15 不允许偏差 Ⅱ类 ≥1.40 Ⅲ类 ≥1.45 （2）每卷段数和最小段长应符合表3规定表 每卷段数 最小段长 ≤25m/卷 ≤4段 ≥1m 25m /卷＞＜ ≤6段 ≥1m ≥40m/卷 ≤8段 ≥1m 1.4.4外观要求 应符合表4 表1-4 序号 项目 要求 1 花纹 较清晰 2 色差，级 ≥3-4 3 平滑性 轻微不平滑 4 脱层、气泡 不允许 5 熔融、脏污、浮斑和皱折等明显分散性缺陷 在1m范围内，缺陷面积不超过0.05㎡，每卷累计缺陷面积不超过0.9㎡ 6 皱折、色道等明显等连续性缺陷 距两侧边缘15cm以内允许一侧出现连续性缺陷；幅宽内允许出现一条缺陷宽度≤3cm的线道 1.4.5 产品物理性能要求 应符合表5规定。 项目 指标 Ⅰ类 Ⅱ类 Ⅲ类 1 表密度g/cm2 ≤0.65 ≤0.65 ≤0.65 2 拉伸负荷N/cm ≥40 ≥50 ≥55 3 断裂伸长率 % ≥20 ≥20 ≥20 4 断裂负荷N ≥20 ≥30 ≥30 5 剥离负荷N/25cm ≥29 \ ≥49 6 肩裂性 高度 mm ≥7 负荷 N ≥49 7 耐折牢度 20万次 无裂纹 2.5万次 无裂纹 8 表面颜色分度级 干摩擦 ≥4 湿摩擦 ≥3 汗液摩擦 \ ≥3 \ 9 湿透度 mg/cm2.h ≥1.5 \ ≥1.5 10 吸水度 ℅ ≥15 \ ≥15 11 耐水度 水压14.7kpa 表面无水珠 12 耐热粘着性 级 ≥4 1.5项目可行性分析 （1）年产200万米聚氨酯合成革项目为中小型项目，投资回收期较短，污染容易控制，投资风险小。根据目前中国聚氨酯合成革生产行业概况分析知其具有很大的可行性。 （2）生产水性聚氨酯合成革浆料的原料国内易得，主要原料国内均可购买到；生产水性聚氨酯合成革浆料的工艺技术路线成熟、可靠，为100℃以内常压操作，设备定型、通用，生产周期短；本工艺生产采用全料进，全