冻融环境下钢筋与粉煤灰混凝土粘结性能.docVIP

冻融环境下钢筋与粉煤灰混凝土的粘结性能 　　摘要：通过对内贴应变片钢筋的直接拔出试验，分析冻融作用下粉煤灰掺量对钢筋与粉煤灰混凝土间粘结性能的影响，得出冻融循环作用对钢筋与粉煤灰混凝土之间粘结性能的影响规律。试验结果表明：钢筋与粉煤灰混凝土的粘结强度随粉煤灰掺量的增加而降低；当粉煤灰掺量一定时，随着冻融循环次数的增加，混凝土强度有所下降，钢筋与粉煤灰混凝土间极限粘结强度降低；当粉煤灰掺量较大，达到40%时，随冻融次数的增加，钢筋粉煤灰混凝土试件极限粘结强度的下降幅度明显减缓，极限粘结强度对应的滑移量增大。表明掺入较多粉煤灰可使试件的冻融损伤现象得到缓解，冻融环境下钢筋混凝土的粘结性能得到提高 关键词：冻融循环；粉煤灰混凝土；直接拔出试验；粘结强度；粘结应力分布 中图分类号：TU375 文献标志码：A 文章编号2015 Abstract：The effect of freeze-thaw cycle to the bonding performance between steel bar and fly ash concrete was analysed through pull-out test to steel bars attached strain gages inside. The results of pull-out test under different number of freeze-thaw cycle show that the bonding strength between steel bar and concrete decrease as the content of fly ash increasing； when the content of fly ash stay the same， with the number of freeze-thaw cycle increasing， the concrete compressive strength decline， and the bonding strength decrease； as the fly ash replacement rate stay 40%， with the number of freeze-thaw cycle increasing， the ultimate bonding strength decreased speed reduce， and the free end displacement corresponding to the ultimate bonding strength increase， which shows that mixed with a large number of fly ash can remit the freeze-thaw damage phenomenon， the bonding performance of reinforced concrete specimens under freeze-thaw environment is improved. Key words：freeze-thaw cycle； fly ash concrete； pull-out test； bonding strength； bonding stress distributing 粉煤灰作为混凝土材料中最为常用的一种矿物掺合料，既可以减少水泥用量，降低混凝土的成本，又可以改善混凝土部分工作性能、力学性能和耐久性[1-2]，能够更好地满足实际工程的需求 在寒冷环境下的混凝土结构会受到冻融侵蚀，冻融作用会使混凝土劣化[3]，劣化后的混凝土与钢筋间的粘结性能将受到影响[4-6]。在影响混凝土结构破坏的因素中，冻融侵蚀对于混凝土结构的破坏程度较大，冻融损伤严重时会导致结构失效[7-9]。钢筋与混凝土间的粘结性能是影响混凝土构件正常使用性能的重要因素之一[10-14]，在混凝土工程中合理利用粉煤灰是否能够发挥其在冻融环境中改善钢筋与混凝土之间的粘结性能尚不明确。Arezoumandi等[15] 研究了粉煤灰掺量大于50%的混凝土试件与钢筋的粘结性能，Costel等[16]对高温养护的粉煤灰混凝土试件的粘结性能开展了试验分析。胡晓鹏等[17]分析了粉煤灰掺量对直接拔出试件与梁式试件中钢筋与粉煤灰混凝土粘结性能的影响，冀晓东等[10]研究了冻融循环作用后钢筋与混凝土的粘结性能，而关于冻融环境下钢筋与粉煤灰混凝土间粘结性能方面可供参考的试验与分析并不多，冻融作用与粉煤灰掺量对钢筋混凝土间粘结性能的影响有待深入研究 通过对