金属涂装预处理技术一些进展.pdfVIP

Anticorrosion Coatings and Application 防腐涂料与涂装 金属涂装预处理技术一些进展 □ 刘国杰 (中国涂料工业协会产业发展部，北京 100079) 摘要：叙述了利用溶胶-凝胶技术制备无机-有机杂化复合涂层的原理和过程，及用于铝合金、不锈 钢、镀锌铁板等金属涂装的预处理，革除磷化、铬钝化等污染工序，获得很好效果。并介绍了对汽车、铝型 材等涂装实例。对低表面处理涂料发展简况和应用实例也作了简介。 关键词：无机-有机杂化；溶胶-凝胶；涂装前处理；锈面涂料；低表面处理 中图分类号：TQ639.1 文献标识码：A 文章编号：1006-2556(2011)10-0004-06 Progress of Pretreatment Technology for Metal Painting Liu Guojie (Department of Industrial Development, China National Coatings Industry Association, Beijing 100101) Abstract:This paper narrates the principle and process for the preparation of organic/inorganic hybrid composite coating through sol-gel technology. The coating is used in the pretreatment of aluminum alloy, stainless steel and galvanized iron sheet, and the processes with pollution including phosphatization and chromium passivation can be removed. The paper introduces the examples used in the painting of automobile and aluminum material and also the development of low surface treatment coatings and the application examples. Keywords:organic/inorganic hybrid, sol-gel, pretreatment, rusted-surface coatings 1 概 述 虽有利于涂料的渗透而增加附着力，但增强防腐性 1.1 金属涂装表面预处理中钝化的重要性 不如钝化膜，钝化膜是用铬酸盐或Cr O （铬酐）氧化， 2 3 金属表面在涂装前必须进行表面处理，使涂料 在金属表面生成一层致密的钝化薄膜，可以进一步 最大限度地发挥其保护与装饰效果[1-2] 。金属涂装前 提高涂料的附着力和防腐蚀性能。金属表面钝化工 表面预处理一般为： 艺早在1900年已问世，在金属涂装中得到了广泛应 [3] 除油→热水洗→冷水洗→酸洗→冷水洗→磷化