590_时效处理对2205双相不锈钢组织与硬度的影响.pdfVIP

32 2 V o.l 32, No. 2 2 0 1 1 6 SHANGHA INONFERROU SMETALS June, 2011 : 1005- 20 6( 2011) 02- 0061- 05 590e 2205 , , , ( , , 20180 ) : 通过对 2205双相不锈钢 590e 的时效行为进行研究, 采用光学显微镜( OM )环境扫描 电镜( ESEM)和透射电镜(TEM), 析时效处理工艺对材料组织的影响规律发现 590e 时效 8h, 开始有中间相析出, 析出相集中在 A相以及 A/C相界通过TEM 物相 析, 发现 590e 时 效析出相有 R相此外, 还研究了时效处理对材料硬度的影响 : 2205双相不锈钢; 时效处理; 组织; 硬度 : TG156. 92 : A EffectsofAgingTreatmentat590e on thePhase Structure and Hardnessof2205Duplex Stainless Steel FAN Jun-we,i HE Chen-chong, DU Chun-feng, YAN Biao (S chool of M aterials Science and Engineering, Tongj i University, ShanghaiK ey Lab of DA f or F nctionalM etallicM aterials, Shangha i201804, China) Abstract: Aging treatment w as applied to 2205 duplex stainless steel samples at 590e . The m icrostructure of these samples w as investigated by optical m icroscopy ( OM ), environmental scann ing electron m icroscope ( ESEM ) and transm ission electron m icroscopy (TEM ). Intermediate phase began to precipitate after aging for 8 h, and the precipitations concentrated in the A phase and the A /C phase boundary. By TEM phase analysis, the precipitationsw ere found to be R phase. The effect of aging treatment on the hardness of 2205 dup lex stainless steelw as also studied. eyWords: 2205 duplex stainless stee;l aging treatment; m icrostructures; hardness , 0 ; 316L 30%, 2205 , 2205 , ; , , ; ,