废旧丁腈胶粉应力诱导脱硫反应的影响因素研究—螺杆转速的影响 摘 要 本文研究了废旧丁腈胶粉应力诱导脱硫反应的影响因素——螺杆转速的影响。论文中采用废旧丁腈胶粉挤出过程中加入线性高分子（如EVA）作为溶胀剂和承载流体，并改变双螺杆挤出机螺杆转速和反应温度的方法研究了过氧化物、多硫化物及其复合促进剂对废旧丁腈胶粉脱硫反应的影响。考察了脱硫促进剂品种、反应温度和双螺杆挤出机螺杆转速对废旧丁腈胶粉脱硫产物凝胶含量的影响。结果表明：螺杆转速在200rpm到1000rpm时，随螺杆转速的提高，凝胶含量呈现先下降后上升的趋势。在复合促进剂DBPH/420/水，挤出温度为180℃，螺杆转速为400rpm时，废旧丁腈胶粉脱硫产物的凝胶含量为45.43%，脱硫效果较好。 关键字：废旧丁腈橡胶 高剪切应力 螺杆转速 脱硫Effects of Shear Stress Coming from the Screw Speed of Twin Screw Extruder on Devulcanization of Waste Nitrile Rubber Abstract This paper studies the waste nitrile rubber powder desulfurization reaction of stress-induced factors - the impact of screw speed .This experiment used nitrile rubber powder is used in the extrusion process to linear polymer ( such as EVA) as the swelling agent and carrier fluid and changing the twin-screw extruder screw speed and the reaction temperature were studied peroxides polysulfides and composite enhancers on waste nitrile rubber powder desulfurization reaction.The effects of different species desulfurization accelerators , twin-screw extruder screw speed and the reaction temperature on desulfurization products nitrile rubber powder content of the gel . The experimental results show that: in the 200rpm to 1000rpm, with the increase in screw speed,gel content values first decreased and then increased, when 400rpm better desulfurization effect. Key Words: WNBR high shear stress screw speed Desulfurization 毕业设计（论文）原创性声明和使用授权说明 原创性声明 本人郑重承诺：所呈交的毕业设计（论文），是我个人在指导教师的指导下进行的研究工作及取得的成果。尽我所知，除文中特别加以标注和致谢的地方外，不包含其他人或组织已经发表或公布过的研究成果，也不包含我为获得 及其它教育机构的学位或学历而使用过的材料。对本研究提供过帮助和做出过贡献的个人或集体，均已在文中作了明确的说明并表示了谢意。 作 者 签 名：　　 　 　　日　 期：　　 　 　　 指导教师签名：　　 　 　　 日　　期：　　 　 　　 使用授权说明 本人完全了解 大学关于收集、保存、使用毕业设计（论文）的规定，即：按照学校要求提交毕业设计（论文）的印刷本和电子版本；学校有权保存毕业设计（论文）的印刷本和电子版，并提供目录检索与阅览服务；学校可以采用影印、缩印、数字化或其它复制手段保存论文；在不以赢利为目的前提下，学校可以公布论文的部分或全部内容。 作者签名：　　 　 　　 日　 期：　　 　 　　 学位论文原创性声明 本人郑重声明：所呈交的论文是本人在导师的指导下独立进行研究所取得的研究成果。除了文中特别加以标注引用的内容外，本论文不包含任何其他个人或集体已经发表或撰写的成果作品。对本文的研究做出重要贡献的个人和集体，均