高频淬火与真空淬火(国外英语资料).docVIP

高频淬火与真空淬火(国外英语资料) High frequency quenching is mostly used for surface quenching of industrial metal parts. It is a kind of metal heat treatment method that causes the workpiece surface to produce a certain induction current, rapidly heats the surface of parts, and then rapidly quenching. Induction heating equipment, that is, the workpiece induction heating, in order to carry out surface hardening equipment. Induction heating principle: the workpiece is put into the inductor, and the inductor is usually a hollow copper tube with middle frequency or high frequency alternating current (1000-300000Hz or higher). Alternating magnetic field induced current to produce the same frequency in the workpiece, the induced current is not uniform in distribution on the surface of workpiece, strong, and in the internal core is weak, to close to 0, the use of the skin effect, can make the rapid heating of the workpiece surface, in a few seconds, the surface temperature rises 800-1000o C, and the core temperature is very small Selection of induction heating frequency: select the frequency according to the requirements of heat treatment and heating depth. The higher the frequency, the shallower the depth of heating. High frequency (more than 10KHZ) heating depth of 0.5-2.5mm, generally used for heating small and medium-sized parts, such as small modulus gear and small shaft parts. Medium frequency (1~10KHZ) heating depth of 2-10mm, generally used for large diameter shaft and large and medium modulus gear heating. Power frequency (50HZ) heating the depth of hardened layer is 10-20mm, generally used for large size parts diathermy, large diameter parts (diameter ? more than 300mm, such as roller surface quenching). The depth of induction hardening surface hardening layer depends on the frequency of alternating current, generally high frequency, shallow heating depth, hardening layer depth is shallow. The relationship between the frequency of F and the heating depth, has the following for