多元合金化双相铸造不锈钢Cr22Ni5Mo4Cu3.docVIP

多元合金化双相铸造不锈钢Cr22Ni5Mo4Cu3.5的组织与性能 　秦紫瑞　郭　宁　郭　珊　潘国强　 摘　要　试验结果表明，所研制的Cr22Ni5Mo4Cu3.5钢，经1 050 ℃×2 h水冷固溶处理后，具有良好的耐均匀腐蚀性能，较好的抗晶间腐蚀与抗点蚀能力。此外，新型钢还具有良好的综合力学性能和工艺性能。关键词　双相　铸造　不锈钢 Structure and Properties of Multicomponent Duplex-Phase Cast Stainless Steel Cr22Ni5Mo4Cu3.5 Qin Zirui and Guo Ning(Dalian University of Technology, Dalian 116023) Guo Shan and Pan Guoqiang(Dalian Acid Prof Pump Works) Abstract　The experimental results show that the developed steel Cr22Ni5Mo4Cu3.5 solid solution treated at 1050 °C for 2 h, water cooled, has excellent uniform corrosion resistance, and better intergranular