粉煤灰的改性及从模拟烟气中吸附脱除SO2试验研究 摘要：研究了粉煤灰改性及脱硫的机理。本试验采用煅烧-水热化合法，对50g粉煤灰进行改性，并用改性后的粉煤灰进行模拟烟气脱硫试验，试验得出，当助熔剂Na2CO3用量12g，Ca(OH)2用量15g，在80℃下水合消化8h，含湿量30%时，改性粉煤灰对SO2的吸附效果较好，此种改性灰的最大吸附率可以达到93.46%，平均吸附率为85.186%。 关键词：粉煤灰；吸附率；改性；SO2 中图分类号：X701.3 文献标志码：A 文章编号： Study on Modification Fly Ash and Absorption of SO2 in Flue Gas Abstract：Studied the mechanism of modification of fly ash and adsorption sulfur dioxide.The test uses calcined-water thermalization method, The results indicate that the optimum modifying conditions for the fly ash of 50g are the flux Na2CO3 amount of 12g, Ca (OH) 2 amount of 15g, temperature of 80℃,digestion time of 8h, moisture content of 30%, under this condition,the maximum adsorption rate of modified ash can reach 93.46%, the average adsorption rate was 85.186%. Keywords:fly ash；adsorption rate；modify；sulfur dioxide 引 言 我国超过85%的煤炭直接用于燃烧过程，大量燃煤导致SO2排放量居高不下。过量排放SO2导致我国空气污染不断加剧，严重危害人类健康。目前，减少燃煤SO2排放量最有效的途径是烟气脱硫。 粉煤灰的组成成分中有SiO2、Al2O3、CaO、Fe2O3和未燃尽炭[1]。粉煤灰中含有大量的多孔物质[2-4],具有较大的比表面积[5-9],且其中的铝、硅及其很多成品均是很好的脱硫剂和吸附剂材料[10-16],因此,利用粉煤灰制备成高性能的吸附材料、脱硫剂等,成为现阶段学术界研究的一大热点。 目前，粉煤灰改性的主要方法有火法和湿法，由于原状粉煤灰吸附SO2效率较差，本试验将火法与湿法并用，采用煅烧-水热化合法将粉煤灰改性，以制备出吸附效率高、吸附容量大的粉煤灰基改性吸附剂，脱除模拟烟气中的SO2。实践证明，此种吸附剂吸附脱除SO2效果明显，可以实现“以废制废”的工业发展理念。 1 粉煤灰改性试验 1.1 粉煤灰改性及脱硫原理 加入助熔剂（Na2CO3）煅烧熔融,会破坏粉煤灰稳定的晶格结构，使其释放出无定型的SiO2和Al2O3等物质，增强粉煤灰的活性，将熔融后的产物再加入Ca(OH)2进行水热化合反应，这一过程涉及的主要反应有： Ca(OH)2+SiO2+H2O→(CaO)x(SiO2)y(H2O)z (1-1) Ca(OH)2+Al2O3+H2O→(CaO)x(Al2O3)y(H2O)z (1-2) Ca(OH)2+Al2O3+SiO2+H2O→(CaO)x(Al2O3)y(SiO2)z(H2O)w (1-3) 该反应产物是种多孔晶体，有较大的比表面积[17]，其脱硫原理是： (CaO)x(Al2O3)y(SiO2)z(H2O)w +SO2+O2→(CaO)x(Al2O3)y(SiO2)z(CaSO4)M(H2O)w (1-4) 上述式中系数X、Y、Z、W、M可取任意值。 1.2试验原料 纯度为99.9%的二氧化硫（SO2、佛山市华特气体有限公司）， 粉煤灰（FA、贵州大方发电有限公司、分析纯），无水碳酸钠（Na2CO3、天津市永大化学试剂有限公司 、分析纯 ），氢氧化钙含量95%以上（Ca(OH)2、天津市科密欧化学试剂有限公司、分析纯）。 粉煤灰主要成分如下： 表1-1粉煤灰主要成分 Table 1-1 fly ash main ingredient % SiO2 Al2O