锰铁合金氧化脱磷研究概况 - 有色金属科学与工程.docVIP

锰铁合金脱磷综述 赖朝彬，习小军，干磊，彭园龙，张真铭，刘庭光 （江西理工大学冶金与化学工程学院，江西 赣州 341000） 摘 要：随着钢铁工业的快速发展，对钢水洁净度的要求日益增高。锰铁合金作为炼钢过程的脱氧剂及合金添加剂，其品位受到冶金界的极大关注。文章主要概述了锰铁合金脱磷渣系的研究现状及其应用于锰铁工业化脱磷中存在的不足，指出了锰铁合金脱磷渣系的开发方向，并重点对含稀土氧化物渣系用于锰铁合金脱磷的可能性进行分析预测。 关键词：锰铁合金；脱磷；稀土氧化物 Review of Dephosphorization for Ferromanganese Alloy LAI Chaobin，XI Xiaojun，GAN Lei，PENG Yuanlong， ZHANG Zhenming，LIU Tingguang (School of Metallurgy and Engineering,Jiangxi University of Science and Technology,Ganzhou 341000,China) Abstract: With the rapid development of iron and steel industry, the steel cleanliness requirements for increasing higher. Ferromanganese alloys as deoxidizer and alloy additive in steelmaking process, its quality has been of great concern to the field of metallurgy. This paper mainly summarizes the research status of ferromanganese alloys dephosphorization slag series and its shortage for applying in the ferromanganese industrialized dephosphorization, pointing out the development direction of ferromanganese alloys dephosphorization slag series, and focus on analysising and forecasting for the possibility for the containing rare earth oxide slag series applys to the ferromanganese alloys dephosphorization. Key words: ferromanganese alloys; dephosphorization; rare earth oxide 0 引 言 锰铁是铁合金中最大的一个系列，也是钢铁生产中消耗量最大的铁合金品种。锰铁主要用作钢铁生产过程的脱氧剂和合金添加剂，其消耗量约为钢总产量的0.8 %~1 %[1]。高炉锰铁磷含量高达0.4 %~0.6 %，必须将磷加以脱除至0.2 %以下，才能满足洁净钢对钢水磷含量的要求。因此，锰铁合金脱磷引起国内外冶金界的极大关注，众多冶金学者进行了这方面的课题研究[2-4]。 收稿日期： 基金项目：国家自然科学基金项目 作者简介：赖朝彬（1964- ）E-mail:lcb5115@126.com. 1 锰铁合金脱磷研究现状 由于高品味的锰矿资源消耗过快，加之钢铁行业对锰铁合金的需求逐步增大，锰铁合金脱磷受到冶金工作者的重视。高炉锰铁中的磷主要来自于锰矿石和焦炭，其带入的磷含量分别占锰铁中总磷含量的65 %及35 %[5]。而据研究表明[2,5]，高炉锰铁冶炼过程中是无法脱磷的，则必须开发能适用于液态锰铁的炉外脱磷方法。目前，锰铁脱磷方法概况起来主要有氧化脱磷和还原脱磷两种。 1.1 锰铁熔体还原脱磷 还原条件下能够实现锰铁合金的脱磷保锰，且脱磷率较高，所以冶金工作者对锰铁合金还原脱磷进行了大量的研究工作[6-22]。还原脱磷是用碱土金属或其合金还原锰铁中的磷，使其生成金属磷化物转移到渣中而去除。常用的脱磷剂有Ca-CaF2、CaC2-CaF2、CaSi-CaF2、Ca-Ba-Si-CaF2(1) 还原脱磷一般要求氧位，故脱磷过程锰不会烧损。目前对液态锰铁还原脱磷研究资料较多，如J.Kr.Tuset等[6]通过热力学数据分析了液态锰铁还原脱磷条件，得出碱金属的磷化物比锰的磷化物更稳定的