难加工材料攻丝摩擦扭矩的试验研究.pdfVIP

2007 年第 41 卷 №11 6 1 难加工材料攻丝摩擦扭矩的试验研究 1 1 2 唐艳丽 　韩荣第 　鞠加彬 1 2 　 哈尔滨工业大学 　 黑龙江省农业工程职业学院 摘 　要 :分析了攻丝过程及退回过程两阶段丝锥的力学特征 ,在此基础上分别建立了切削扭矩和摩擦扭矩力 学模型 。针对难加工材料 GH4169 和 TC4 ,采用 M6 标准丝锥进行攻丝试验 。结果表明:摩擦扭矩 占攻丝扭矩的比 率分别为 45 %和 55 % ;针对 45 钢 ,摩擦扭矩则很小 。可见 ,摩擦扭矩大是 GH4169 和 TC4 攻丝困难的主要原因。 关键词 :切削力 , 　摩擦力 , 　切削扭矩 , 　摩擦扭矩 Experimental Investigation of Friction Torque for Tapping Hardtocut Materials Tang Yanli 　Han Rongdi 　Ju Jiabin Abstract : Based on the analysis of tap mechanics feature in both cutting and withdrawal process , the mechanical models of tapping moment of torque and friction one were created respectively in the paper . The standard tap of an outer diameter of M6 was utilized for tapping difficulttomachine materials of GH4169 and TC4 . The test results indicated that the leading cause of difficult tapping in GH4169 and TC4 was the largeness of their friction torques which was about 45 % and 55 % of tapping torque respec tively but a lesser percentage for 45 steel . Keywords :tapping forces , 　friction forces , 　tapping torque , 　friction torque 外 ,螺纹扣的弹性后效会产生相当大的正压力 ,能把 　　1 　引言 丝锥齿夹在螺纹底部 ,并使攻丝扭矩增大[2 ] 。国内 攻丝是小直径内螺纹加工的常用方法 ,对高温 外学者大多从刀具材料及其表面处理 、加工参数 、冷 合金 GH4 169 和钛合金 TC4 等难加工材料 ,存在丝 却润滑济及金属离子添加济等[3～5 ] 方面着手来研究 锥易折断、螺纹质量差 、生产效率低等问题[ 1] 。这是 难加工材料的切削加工过程 , 以减小切削过程中的 因为用标准丝锥攻螺纹时 ,刀齿与工件接触面积大 ,