GCr15轴承钢盘条高线工艺开发.pdfVIP

GCr15轴承钢盘条高线工艺开发 d o i ：10.3969/j .issn .1006-110X .2016.04.011 GCr15轴承钢盘条高线工艺开发 刘学森 (天津钢铁集团有限公司，天津300301 ) [摘 要 ]为满足使用要求，通过研究加热、控轧控冷工艺、重新设定工艺参数、控制表面质量等措施，使用150 mm x 150 m m 的连铸坯开发出轴承钢GCr 1 5 盘条。该盘条的金相组织、表面脱碳层、碳化物不均勻性及表面质量等 各项指标良好，可满足国家标准要求,且能够保证产品的加热质量，实现安全生产。 [关 键 词 ]轴 承 钢 ；盘条；高线;碳化物；工艺 Development of Productive Process for High Speed Wire Rod of GCr15 Bearing Steel LIU Xue-sen (Tianjin Iron and Steel Group Co., Ltd., Tianjin 300301, China) Abstract In order to meet application demand, the wire rod of GCr15 bearing steel produced by 150 mm 伊 150 mm slab was developed by measures of studying heating and controlled rolling and cooling process, re­ setting process parameters and controlling surface quality. Indices of the said wire rod, such as metallographic structure, surface decarburization layer, carbide non-uniformity and surface quality, could meet the require­ ment by the national standard. The heating quality of the product was ensured and safe production realized. Key words bearing steel; wire rod; high speed wire rod; carbide; process i 引言 过 长 ，加热方式为蓄热式烧嘴和换向系统组成的两 轴 承 钢 GCr15盘条一般用 于 轴 承 滚 针 、滚珠的 端 加 热 ，存 在 炉 内 两 端 温 度 高 于 炉 内 中 间 的 情 况 ， 生 产 。为 了 满 足 强 韧 性 能 、抗疲劳性能和耐磨性能 使 得 坯 头 温 度 过 高 ，导 致 在 加 热 时 坯 头 下 弯 ，难以 的 要 求 ，对内在质量要求较高。轴 承 钢 含 碳 量 高 ，在 出 钢 ，从 而 引 发生产事故。而加热温度较低时又会 连铸过程中会不同程度地析出碳化物。有研究表明 引起碳化物不均勻难以消除的问题。为 此 ，通过加 这 种 碳 化 物 的 不 均 勻 性 对 轴