镝添加对Mg-4Y-3Nd-0.4Zr合金组织和力学性能的影响.pdfVIP

Trans. Nonferrous Met. Soc. China 27(2017) 797−803 Effect of Dy addition on microstructure and mechanical properties of Mg−4Y−3Nd−0.4Zr alloy 1,2 1,2 1,3 4 Hong-hui LIU , Zhi-liang NING , Jun-ying YI , Qian MA , Hai-chao SUN1,2, Yong-jiang HUANG 1,2, Jian-fei SUN1,2 1. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China; 2. National Key laboratory for Precision Hot Processing of Metals, Harbin Institute of Technology, Harbin 150001, China; 3. School of Materials Science and Engineering, Jiangsu University of Science and Technology, Zhangjiagang 215600, China; 4. Mechanical and Manufacturing Engineering and Design Research Institute, School of Aerospace, RMIT University, GPO Box 2476, Melbourne, VIC 3001, Australia Received 25 January 2016; accepted 26 August 2016 Abstract: Minor Dy element was added into a Mg−4Y−3Nd−0.4Zr alloy, and its effects on the microstructure and the mechanical properties at elevated temperatures were investigated. Scanning electron microscope (SEM) and transmission electron microscope (TEM) were used to observe the microstructures. The results indicated that the as-cast eutectic and isolated cuboid-shaped Mg−RE phases were Mg RE and Mg RE , respectively, and distributed mainly along grain boundaries. After a solution treatment, the 5 3 17 eutectic Mg RE phases were dissolved into t