t23焊接的.doc

SA213-T23钢焊接性分析 洪卫1，王志伟1，高义斌2 （1. 山西电建三公司，山西太原 030041；2. 山西电力科学研究院，山西太原 030001） 摘要： 采用了焊丝对钢的焊接性进行了研究，测试了焊接接头在常温下的力学性能，对焊缝金属WM和热影响区HAZ进行微观组织观察分析。发现氧化物等杂质容易聚集在热影响区，极易在焊缝根部形成规范参数大容易引起焊缝区未熔合，在启裂处有脆性断裂迹象。通过分析对钢的焊接性及工艺规范有了更清楚的认识，为大参数火电机组和核电机组材料的焊接具有一定的帮助。Weldability analyses of SA213-T23 steel Hong Wei1, Wang Zhiwei1, Gao Yibin2 (1. Shanxi №3 Power Construction Company, Shanxi Taiyuan 030041 2. Shansi electric power establishment, Shanxi Taiyuan 030001) Abstract: The weldability of SA213—T23 which was welded with 2CrWV wires was discussed. the mechanical property of The weld joint was tested at ordinary temperature and the microstructure of weld metal and HAZ was analysed. The oxides gathered easily around HAZ, the oxygenation formed at the root of weld easily if welding speed was unsuitable. Lack of fusion was formed at weld zone if parameter went far, brittle rupture happened at open split department. The weldability and technical regime of SA213 - T23 were recognized, which was useful for the welding of thermal power set with big swifts parameter and nuclear power set stuff. Key words: T23, Weldability, Analyses 0、 引言 王曲工程2号机组为装机容量600 MW超临界火力发电机组，锅炉出口压力23.7 MPa，锅炉岛所涉及的钢材包括SA106C、T/P12、P22、SA213—T23、T/P91等，规格从φ26.7×7.8至φ610×100，共50余种，锅炉本体受热面范围内的高压焊口达四万余道，在锅炉岛的低温过热器立式部分和水平段的第一、二两层选用的钢材为SA213-T23钢，规格为φ51×6.5mm，管排之间的距离为50 mm，管子的施焊焊口最小间距为5 mm，该部件共有此类焊口为760道，此钢种不仅特殊，且没有现成的工艺，如不尽快找到解决这个问题的办法，将严重影响焊接施工的顺利进展。 1、 焊接性能分析 SA213—T23钢是日本研制的新钢种，在T22（2.25Cr-1Mo）钢的基础上降低了含碳量和含Mo量，添加1.6%的W，并添加了微量的Ni、V、N、B，改进成为T23。由表1可看出T23钢含碳量的降低，提高了钢材的可焊性，而微量元素的添加，又大大提高了钢材的高温蠕变强度。 表1 SA213—T23钢样管的化学成分表 % C Mn Si Cr Mo V Nb W B S P 0.06 0.51 0.23 2.1 0.14 0.219 0.033 1.618 0.0016 0.002 0.01 1.1、 淬硬性 钢材的淬硬性取决于它的含碳量、合金成分以及合金成分的含量。这里我们首先采用焊接性间接估算法，按照钢材碳当量公式： Ceq（JIS）=C+Mn/6+Si/24+Ni/40+Cr/5+Mo/4+V/14（%）=0.06+0.51/6+0.23/24+2.1/5+0.14/4+0.219/14=0.63（%）＞0.4% 由此可以判断此钢材有一定的淬硬性，并且SA213—T23钢中的主要合金元素Cr、Mo、V等都可以不同程度地提高钢材的淬硬性，推迟了钢在冷却过程中的转变，提高了过冷奥氏体的稳定