攀钢冷轧厂RuthnerFe2O3粉制取高档永磁铁氧体材料的研究.pdfVIP

2007年l2月 四川有色金属 Sichuan Nonferrous Metals ·29 · 文章编号：1006—4079(2007)04—0029—03 攀钢冷轧厂Ruthner Fe203粉制取高档永磁铁 氧体材料的研究 王彦华 (攀枝花钢铁研究院，四川 攀枝花617000) 摘要：考察了攀钢冷轧厂Ruthner Fe203粉理化性能，研究了用Ruthner Fe203粉制 备永磁铁氧体的预烧工艺、摩尔比、烧结温度等工艺制度，制取的永磁铁氧体磁性能 达到或超过SJr／T10410—93标准中的Y30H—l牌号水平。 关键词：Ruthner工艺；Fe203粉；永磁铁氧体 中图分类号：TF12 文献标识码：A Research on Preparation of High Grade Permanent Magnet Ferrite from Ruthner Fe203 Powder Supplied from Pangang Cold Rolling Mill WANG Yan．hua (Panzhihua Iron and Steel Research InstitutP。P口nzhihua。Sichuan 617000) Abstract：An investigation was made into the physical and chemical properties of the Ruthner Fe203 powder supplied from Pangang Cold Rolling Mil1．Process schemes such as prefiring，mol ratio，sintering temperature for preparing permanent magnet ferrite from Ruthner Fe203 powder was researched．The permanent magnet ferrite made by this process exhibits better performance than Y30H一1 grade under SJ／T10410——93 standard． Key words：Ruthner process；Fe203 powder；permanent magnet ferrite 吨。在永磁铁氧体的原材料中，Feb03粉含量约 0 引 言 占90％，因此，磁材工业迫切需要大量的优质稳 随着科学技术的不断发展，电子工业的重要 定的Fe20 粉原料，以生产高性价比的磁性材料。 基础材料之一的磁性材料发展很快，尤其是独具 攀钢冷轧厂酸回收系统，以钢板酸洗液为原 储能和节能特点的永磁铁氧体材料发展势头更是 料，采用Ruthner喷射雾化焙烧技术，获得再生盐 迅猛。摩托车、汽车工业、家用高档电器、信息产 酸及Ruthner Fe203粉。为使攀钢Ruthner Fe203 业等应用领域对高剩磁(Br)、高娇顽力(}{ci)、高 粉更广泛地应用于磁性材料工业，作者就 Fe2O3 磁能积((BH) )的磁性材料的强劲需求极大地 粉制造高性能永磁铁氧体的工艺制度进行了系统 推动永磁铁氧体材料及相关产业的发展，高性能、 研究。结果表明，攀钢 Ruthner Fe20 粉可生产 新牌号磁性材料产品不断涌现。我国是磁性材料 Y30BH、Y30H—l、Y32等高性能牌号的永磁铁 的生产和出口大国，年产永磁铁氧体达20余万 氧体材料