冲压缺陷及其防止 Stamping defects and prevent the 2010-10-19 17:10:13| classification: metal stamping | Tags: | name and subscription. 1. what kinds of stamping defects are divided into? Stamping production is divided into cutting and forming two categories. The separation process of the deformation is confined to the incision area, with shear deformation, accompanied by tearing (due to the existence of clearance), all with the sheet separation as the main purpose; if the overall deformation is considered to be defective or deformation of the deformation process of waste. Large (some distributed in the part), if broken, that is a waste. 1.1 defects in the separation process 1.1.1 fracture defects, such as fracture and plate surface are not vertical (cone); roughness, high Ra (tear zone), there are flying edges and burrs.. 1.1.2 overall defects, such as the size of the poor, the location is not allowed (mainly refers to the punching type), shape defects, such as round, collapse angle, warping and distortion, etc. 1.2 deformation process defects 1.2.1 is the shape of the product, such as surface uneven, ridge is not clear, wrinkling, distortion, the drum surface (including plastic and elastic), lack of meat. 1.2.2 parts are not qualified in size 1.2.3 geometric position between the unqualified, such as asymmetry, non parallel, non vertical and non concentric, and so on 1.2.4 surface quality, such as picking, orange peel and slip lines. 1.2.5 local fracture and crack 2. what are the factors that affect the quality of stamping? The quality problems in stamping production can be included: 2.1 quality of parts design 2.2 quality of process design 2.3 mold design and manufacturing quality 2.4 press and mould installation, adjust quality 2.5 the chemical composition, mechanical properties, metallographic and surface quality of the sheet 2.6 the quality of the billet, such as shape, size and fracture, etc. if it belongs to multiple drawing, the blank refers to the parts of the inter