填埋场涂层损失的计算.docVIP

生活垃圾卫生填埋场HDPE膜的铺设与工程损耗计算 上海环境工程技术有限公司, 上海，200070 摘要：高密度聚乙烯（HDPE）土工膜已广泛用作生活垃圾填埋场的防渗衬里，以避免对地下水的污染和环境的损害。HDPE土工膜的铺设，在整个生活垃圾卫生填埋场的建设成本中占有显著地位，对其的工程损耗量计算，具有重要的经济意义。因此，本文从垃圾填埋场铺设防渗膜工程的角度，得出HDPE铺膜的损耗率为3.5%-5.0％左右，可以为填埋场防渗膜铺设工程的膜消耗量提供参考。 关键词： 生活垃圾 HDPE膜 损耗 卫生填埋场 The calculation of HDPE membrane engineering loss in municipal solid waste sanitary landfill lining system Shanghai Environmental Engineering Technology Co., Ltd., Shanghai, 200070 Abstract: High Density Polyethylene Impermeable (HDPE) membrane was widely used as liner in the municipal solid wastes sanitary landfill to prevent pollution of groundwater and environment. The fee of HDPE membrane is the main part of the total cost of municipal solid waste sanitary landfill, and thus the calculation of HDPE membrane engineering loss is prerequisite and meaningful. In this paper, we proposed that the engineering loss of HDPE is ranged from 3.5~5.0% based on geomembrane laying works, and this result can be used to estimate the HDPE membrane consumption practically in landfill. Key word: municipal solid waste, HDPE, engineering loss, sanity landfill 1 前言 根据2004年6月1日起实施的建设部最新颁布的行业标准《生活垃圾卫生填埋技术规范》（CJJ17-2004）的强制性条文规定要求：“填埋场必须进行防渗处理，防止对地下水和地表水的污染，同时还应防止地下水进入填埋区”。填埋区防渗主要有天然防渗和人工防渗系统，天然粘土防渗要求其渗透系数不大于1.0×10-7cm/s。对于达不到防渗系数要求的填埋库区须采用铺设高密度聚乙烯（HDPE）土工膜作为防渗衬里。目前，填埋场的防渗膜铺设工程越来越多，由于国家相关的建设工程定额中还没有对填埋场防渗膜铺设有相关的规定，因此，填埋场的防渗膜铺设的工程量需要有一个统一的计算口径来进行规范，本文就防渗膜实际铺设中的一些经验结合工程预算对防渗膜铺设的损耗进行一些探讨。 2 试验材料选择 适于做卫生填埋场衬垫的材料主要有两大类，一类是无机材料，一类是有机材料。常用的无机材料有粘土、水泥澎润土等；常用的有机材料有沥青、橡胶、聚乙烯、聚氯乙烯等。衬垫材料的选择与许多因素有关，如待处理垃圾的性质、场地的水文地质条件、场地的级别、场地的使用年限、覆盖材料的来源以及建设费用等。 目前，天然粘土防渗衬垫已经不再普遍使用了。在天然土层不能满足防渗要求的前提下，填埋场均采用铺设柔性膜防渗。柔性膜有多种材料，目前最广泛使用的填埋场防渗材料是高密度聚乙烯（HDPE）材料，其厚度有1.0mm、1.25mm、1.5mm、2.0mm、2.5mm等几种，它具有如下特点：①HDPE膜具有很强的防渗性能，渗透系数达到10-12cm/s；②化学稳定性好，具有较强的抗腐蚀性能，耐酸、碱及抗老化能力，一般来说，抗化学腐蚀能力是衬垫设计中最需要注意的，而HDPE是所有土工膜中抗化学能力最强的一种，生活垃圾渗滤液不会对HDPE组成的衬垫造成腐蚀，此外，HDPE膜的抗紫外线老化能力强，添加的碳黑可增强对紫外线的防护，而且由于在HDPE土工膜中不允许添加增塑剂，因此不必担心由于紫外线照射而引起增塑剂的挥发；③机械强度高，具有较强的弹性，其屈服伸长率为13%，当伸长率达到700%以上