工业纯铁表面自纳米化及其表征 - 中南大学学报.pdfVIP

42 1 () Vol.42 No.1 2011 1 Journal of Central South University (Science and Technology) Jan. 2011 1, 2 1 1 1 1 (1. 400044 2. 401331) (High energy shot peening, HESP) X HESP 1 mm 0.6 MPa5 cm 10 µm (HV)296.61 min 68.4 nm0.050% 14 min 28.5 nm 0.175% TG142.71 A 1672−7207(2011)01−0062−05 Surface self-nanocrystallization of commercial iron and its characterization 1, 2 1 1 1 1 SUN Jian-chun , SHENG Guang-min , WANG Yue-tian , LU Hao , HAN Jing (1. College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China; 2. College of Metallurgy and Materials Engineering, Chongqing University of Science and Technology, Chongqing 401331, China) Abstract: The commercial iron was successfully surface nanocrystallizated with high energy shot peening (HESP) method. The performance and microstructure of self-surface nanocrystalline layer on the commercial iron were studied and analyzed through microscope observation, scanning electron microscopy (SEM) analysis, microhardness test and X-ray diffraction (XRD) analysis. The results indicate that a nanocrystalline layer of commercial iron can be obtained by HESP method with the following parameters: with 1 mm diameter cast iron shotting ball, 0.6 MPa shotting press and 5 cm distance between the air shotting gun and the sample. The th